The Characterization of Oyster Shell (Crassostrea gigas) as Adsorbent in The Removal of Cr(VI) Ions. A Study of NaOH and H2SO4 Activation Effect

Elkawnie · Vol. 6 No. 1 (2020) · hlm. 77–84

DOI
10.22373/ekw.v6i1.5543
ISSN
2460-8912, 2460-8920
Terbit
2020-06-30
Penerbit
Faculty of Science and Technology Universitas Islam Negeri Ar-Raniry
Bahasa
eng

Abstrak

Abstract: Oyster shell as one of the highest bio-waste in Alue Naga Aceh Besar District, Indonesia, was used as an adsorbent to remove a heavy metal Cr (VI) ion. The study was started by calcinating oyster shells at a high temperature of 800 ºC for 3 hours. The effect of various acid (H2SO4) and base (NaOH) activator was studied using characterization and adsorption experiments. The characterization obtained the sample activated by 10% NaOH (Na10-ACT) and 10% H2SO4 (H10-ACT) had the highest surface area which had 14.23 m2/g, 10.77 m2/g, respectively. Furthermore, the adsorption experiments confirmed the highest surface area by showing the highest Cr (IV) ion removal of 57.66%, 70.7%, respectively. The further investigation using X-ray fluorescence (XRF) determined that the Na10-ACT adsorbent has a better composition compared to the H10-ACT due to its high purities.Abstrak: Cangkang tiram sebagai salah satu bio-limbah padat di Desa Alue Naga Kabupaten Aceh Besar, digunakan sebagai adsorben untuk menghilangkan ion logam berat Cr (IV). Penelitian ini diawali dengan mengkalsinasi cangkang tiram pada temperatur tinggi 800ºC selama tiga jam. Pengaruh penambahan aktivator asam (H2SO4) dan basa (NaOH) juga dipelajari melalui karakterisasi dan pengujian adsorpsi. Hasil karakterisasi menunjukkan sampel yang diaktivasi dengan 10% NaOH (Na10-ACT) dan 10% H2SO4 (H10-ACT) memiliki luas permukaan tertinggi yaitu 14,23 m2/g, 10,77 m2/g, masing-masing. Lebih lanjut, pengujian adsorpsi juga mendukung luas permukaan yang tinggi dengan menghilangkan ion Cr (IV) sebesar 57,66%, 70,7%, masing-masing. Investigasi melalui analisa XRF menyimpulkan bahwa Na10-ACT memiliki komposisi yang lebih baik dibanding H10-ACT karena memiliki kemurnian yang tinggi.

Kata kunci

Jaringan kolaborasi para penulis

40 penulis · 159 tautan kepenulisan bersama · 1 lintas organisasi · menampilkan 40 yang paling banyak terhubung

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • Politeknik Negeri Ujung Pandang
  • Politeknik Negeri Sriwijaya
  • Universiti Brunei Darussalam
  • Afiliasi tidak diketahui
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Jamrud AminuddinAfiliasi tidak diketahui4
Sri Yuliani MAfiliasi tidak diketahui2
Kusmuriyanto KusmuriyantoAfiliasi tidak diketahui2
Reni Ria Armayani HasibuanAfiliasi tidak diketahui2
Malahayati MalahayatiPoliteknik Negeri Sriwijaya2
Anjar Purba AsmaraAfiliasi tidak diketahui2
Agustina WidiyaniAfiliasi tidak diketahui2
Yenni MulyaniAfiliasi tidak diketahui2
Amir AwaluddinAfiliasi tidak diketahui2
Hendri WidiyandariAfiliasi tidak diketahui2
Arnelli ArnelliAfiliasi tidak diketahui2
Wahyu RamadhanAfiliasi tidak diketahui2
Sri ApriliaAfiliasi tidak diketahui2
Nur HidayahPoliteknik Negeri Ujung Pandang1
Muh. AhyarPoliteknik Negeri Ujung Pandang1
Novita Putri FatmaAfiliasi tidak diketahui1
Denisa Putri MaulaniAfiliasi tidak diketahui1
nurjanah nurjanahAfiliasi tidak diketahui1
Agus SupriyantoAfiliasi tidak diketahui1
Sihono SihonoAfiliasi tidak diketahui1
Bagus Sediadi Bandol UtomoAfiliasi tidak diketahui1
Subaryono SubaryonoAfiliasi tidak diketahui1
Ellya SinuratAfiliasi tidak diketahui1
Fateha FatehaAfiliasi tidak diketahui1
Theresia Dwi SuryaningrumAfiliasi tidak diketahui1
Dina FransiskaAfiliasi tidak diketahui1
Bakti Berlyanto SedayuAfiliasi tidak diketahui1
Waryanto WaryantoAfiliasi tidak diketahui1
Hafidz Maulana FadillahAfiliasi tidak diketahui1
Alief Laily MuzayyanahAfiliasi tidak diketahui1
Muhammad Roil BiladUniversiti Brunei Darussalam1
Ratna RatnaAfiliasi tidak diketahui1
Nasrul ArahmanAfiliasi tidak diketahui1
Amri AminAfiliasi tidak diketahui1
Ulfia HumairaAfiliasi tidak diketahui1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://jurnal.ar-raniry.ac.id/index.php/elkawnie/oai, pertama di-harvest 7 Nov 2026, terakhir terlihat 8 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en">The Characterization of Oyster Shell (Crassostrea gigas) as Adsorbent in The Removal of Cr(VI) Ions. A Study of NaOH and H2SO4 Activation Effect</dc:title>
	<dc:creator xml:lang="en">Handayani, Lia</dc:creator>
	<dc:creator xml:lang="en">Rahmawati, Cut</dc:creator>
	<dc:creator xml:lang="en">Nurhayati, Nurhayati</dc:creator>
	<dc:creator xml:lang="en">Astuti, Yayuk</dc:creator>
	<dc:creator xml:lang="en">Darmawan, Adi</dc:creator>
	<dc:subject xml:lang="en">Adsorbent</dc:subject>
	<dc:subject xml:lang="en">BET</dc:subject>
	<dc:subject xml:lang="en">Chromium</dc:subject>
	<dc:subject xml:lang="en">Oyster Shells</dc:subject>
	<dc:subject xml:lang="en">XRF</dc:subject>
	<dc:description xml:lang="en">Abstract : Oyster shell as one of the highest bio-waste in Alue Naga Aceh Besar District, Indonesia, was used as an adsorbent to remove a heavy metal Cr (VI) ion. The study was started by calcinating oyster shells at a high temperature of 800 ºC for 3 hours. The effect of various acid (H2SO4) and base (NaOH) activator was studied using characterization and adsorption experiments. The characterization obtained the sample activated by 10% NaOH (Na10-ACT) and 10% H2SO4 (H10-ACT) had the highest surface area which had 14.23 m2/g, 10.77 m2/g, respectively. Furthermore, the adsorption experiments confirmed the highest surface area by showing the highest Cr (IV) ion removal of 57.66%, 70.7%, respectively. The further investigation using X-ray fluorescence (XRF) determined that the Na10-ACT adsorbent has a better composition compared to the H10-ACT due to its high purities.Abstrak : Cangkang tiram sebagai salah satu bio-limbah padat di Desa Alue Naga Kabupaten Aceh Besar, digunakan sebagai adsorben untuk menghilangkan ion logam berat Cr (IV). Penelitian ini diawali dengan mengkalsinasi cangkang tiram pada temperatur tinggi 800ºC selama tiga jam. Pengaruh penambahan aktivator asam (H2SO4) dan basa (NaOH) juga dipelajari melalui karakterisasi dan pengujian adsorpsi. Hasil karakterisasi menunjukkan sampel yang diaktivasi dengan 10% NaOH (Na10-ACT) dan 10% H2SO4 (H10-ACT) memiliki luas permukaan tertinggi yaitu 14,23 m2/g, 10,77 m2/g, masing-masing. Lebih lanjut, pengujian adsorpsi juga mendukung luas permukaan yang tinggi dengan menghilangkan ion Cr (IV) sebesar 57,66%, 70,7%, masing-masing. Investigasi melalui analisa XRF menyimpulkan bahwa Na10-ACT memiliki komposisi yang lebih baik dibanding H10-ACT karena memiliki kemurnian yang tinggi.</dc:description>
	<dc:publisher xml:lang="en">Faculty of Science and Technology Universitas Islam Negeri Ar-Raniry</dc:publisher>
	<dc:date>2020-06-30</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://jurnal.ar-raniry.ac.id/index.php/elkawnie/article/view/5543</dc:identifier>
	<dc:identifier>10.22373/ekw.v6i1.5543</dc:identifier>
	<dc:source xml:lang="en">Elkawnie; Vol. 6 No. 1 (2020); 77-84</dc:source>
	<dc:source>2460-8912</dc:source>
	<dc:source>2460-8920</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://jurnal.ar-raniry.ac.id/index.php/elkawnie/article/view/5543/pdf_1</dc:relation>
	<dc:relation>https://jurnal.ar-raniry.ac.id/index.php/elkawnie/article/view/5543/10832</dc:relation>
	<dc:rights xml:lang="en">Copyright (c) 2020 Lia Handayani, Cut Rahmawati, Nurhayati Nurhayati, Yayuk Astuti, Adi Darmawan</dc:rights>
</oai_dc:dc>