The Effect of Chemical Activation Using Base Solution With Various Concentrations Towards Sarulla Natural Zeolite

Elkawnie · Vol. 6 No. 1 (2020) · hlm. 85–95

DOI
10.22373/ekw.v6i1.6913
ISSN
2460-8912, 2460-8920
Terbit
2020-06-30
Penerbit
Faculty of Science and Technology Universitas Islam Negeri Ar-Raniry
Bahasa
eng

Abstrak

Abstract: Material characteristics analysis of Sarulla natural zeolite (SNZ) with base activation has been carried out. The base used was NaOH at various concentrations; 0.2 M, 0.5 M, and 2 M. Base activated catalysts were characterized by X-ray Fluorescence (XRF), X-ray diffractometer (XRD), Fourier-transform Infrared (FTIR) Spectroscopy, Scanning Electron Microscopy (SEM) and gas adsorption analysis using BET method. The procedures applied have caused differences in adsorption and desorption rates as well as the crystallinity values of the catalytic materials. Moreover, the ratio of Si/Al contents has also changed at the lowest concentration. On the other hand, the crystallinity of catalysts has decreased at the highest concentration of base applied. The results are reinforced in FTIR characterization which shows the changes of silanol bonds to become silicate and aluminate. Furthermore, morphological analysis of the catalysts shows that homogenous surface was obtained at low concentration, while rough/lumpy surfaces was obtained at higher concentration.Abstrak: Analisis terhadap karakteristik material dari zeolit alam Sarulla (SNZ) dengan metode aktivasi basa telah dilakukan. Basa yang digunakan ialah NaOH dengan berbagai konsentrasi; 0,2 M; 0,5 M, dan 2 M. Katalis yang telah diaktivasi dengan basa kemudian dikarakterisasi dengan Analisis X-ray Fluorescence (XRF), X-ray diffractometer (XRD), Fourier-transform Infrared (FTIR) Spectroscopy, Scanning Electron Microscopy (SEM) dan Gas Adsorption menggunakan metode BET. Dari hasil penelitian, ditemukan perbedaan pada tingkat adsorpsi dan desorpsi, begitu juga dengan kristalinitas pada material katalis. Lebih jauh, rasio konten Si/Al juga berubah pada basa dengan konsentrasi terendah. Di sisi lain, tingkat kristalinitas dari katalis mengalami penurunan pada basa dengan konsentrasi tertinggi. Hasil ini diperkuat dengan data FTIR yang menunjukkan perubahan ikatan silanol menjadi silikat dan aluminat. Lebih jauh, analisis morfologi pada katalis menunjukkan bahwa permukaan yang homogen didapatkan dari penggunaan basa dengan konsentrasi rendah. Sebaliknya, basa dengan konsentrasi tinggi memberikan bentuk permukaan katalis yang tidak homogen serta kasar.

Kata kunci

Jaringan kolaborasi para penulis

40 penulis · 111 tautan kepenulisan bersama · 41 lintas organisasi · menampilkan 40 yang paling banyak terhubung

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • State University of Medan
  • Universitas Sumatera Utara
  • Universitas Gadjah Mada
  • National Research and Innovation Agency
  • University of Palangka Raya
  • Universitas Sains Cut Nyak Dhien
  • Universitas Sari Mutiara Indonesia
  • Organisasi lain
  • Afiliasi tidak diketahui
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Mei RahmaniState University of Medan1
Ekin Dwi Arif KurniawanState University of Medan1
Dimas RidhoState University of Medan1
Elisa PutriUniversitas Sains Cut Nyak Dhien1
Averroes Fazlur Rahman PiliangUniversitas Sumatera Utara1
Kerista TariganUniversitas Sumatera Utara1
Syahrul HumaidiUniversitas Sumatera Utara1
Diana Alemin BarusUniversitas Sumatera Utara1
Junifa Layla SihombingState University of Medan1
Muhammad Abimansyah SaragihState University of Medan1
Muhammad Irvan HasibuanState University of Medan1
Loren SimangunsongState University of Medan1
Marpongahtun MarpongahtunUniversitas Sumatera Utara1
Rufina PramuditaUniversitas Sumatera Utara1
Amru DaulayUniversitas Sumatera Utara1
Vivi PurwandariUniversitas Sari Mutiara Indonesia1
Rezwan Mulya SipahutarState University of Medan1
Eddiyanto EddiyantoState University of Medan1
Nurfajriani NurfajrianiState University of Medan1
Herlinawati HerlinawtatiState University of Medan1
Irwana NainggolanUniversitas Sumatera Utara1
Andriayani AndriayaniAfiliasi tidak diketahui1
Nessa Gina SoniaAfiliasi tidak diketahui1
Nessa Gina SoniaUniversitas Sumatera Utara1
Aldino Javier SaviolaUniversitas Gadjah Mada1
Karna WijayaUniversitas Gadjah Mada1
Latifah HauliNational Research and Innovation Agency1
Marini Fairuz VebryanaUniversitas Gadjah Mada1
Niko PrasetyoUniversitas Gadjah Mada1
Wahyu Dita SaputriNational Research and Innovation Agency1
Amalia Kurnia AminNational Research and Innovation Agency1
Tien Wiati SurjonoBandung Institute of Technology1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://jurnal.ar-raniry.ac.id/index.php/elkawnie/oai, pertama di-harvest 7 Nov 2026, terakhir terlihat 8 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en">The Effect of Chemical Activation Using Base Solution With Various  Concentrations Towards Sarulla Natural Zeolite</dc:title>
	<dc:creator xml:lang="en">Gea, Saharman</dc:creator>
	<dc:creator xml:lang="en">Haryono, Agus</dc:creator>
	<dc:creator xml:lang="en">Andriayani, Andriayani</dc:creator>
	<dc:creator xml:lang="en">Sihombing, Junifa Layla</dc:creator>
	<dc:creator xml:lang="en">Pulungan, Ahmad Nasir</dc:creator>
	<dc:creator xml:lang="en">Nasution, Tiamina</dc:creator>
	<dc:creator xml:lang="en">Rahayu, Rahayu</dc:creator>
	<dc:creator xml:lang="en">Hutapea, Yasir Arafat</dc:creator>
	<dc:subject xml:lang="en">Sarulla natural zeolite</dc:subject>
	<dc:subject xml:lang="en">Base activation</dc:subject>
	<dc:subject xml:lang="en">Crystallinity</dc:subject>
	<dc:description xml:lang="en">Abstract : Material characteristics analysis of Sarulla natural zeolite (SNZ) with base activation has been carried out. The base used was NaOH at various concentrations; 0.2 M, 0.5 M, and 2 M. Base activated catalysts were characterized by X-ray Fluorescence (XRF), X-ray diffractometer (XRD), Fourier-transform Infrared (FTIR) Spectroscopy, Scanning Electron Microscopy (SEM) and gas adsorption analysis using BET method. The procedures applied have caused differences in adsorption and desorption rates as well as the crystallinity values of the catalytic materials. Moreover, the ratio of Si/Al contents has also changed at the lowest concentration. On the other hand, the crystallinity of catalysts has decreased at the highest concentration of base applied. The results are reinforced in FTIR characterization which shows the changes of silanol bonds to become silicate and aluminate. Furthermore, morphological analysis of the catalysts shows that homogenous surface was obtained at low concentration, while rough/lumpy surfaces was obtained at higher concentration.Abstrak : Analisis terhadap karakteristik material dari zeolit alam Sarulla (SNZ) dengan metode aktivasi basa telah dilakukan. Basa yang digunakan ialah NaOH dengan berbagai konsentrasi; 0,2 M; 0,5 M, dan 2 M. Katalis yang telah diaktivasi dengan basa kemudian dikarakterisasi dengan Analisis X-ray Fluorescence (XRF), X-ray diffractometer (XRD), Fourier-transform Infrared (FTIR) Spectroscopy, Scanning Electron Microscopy (SEM) dan Gas Adsorption menggunakan metode BET. Dari hasil penelitian, ditemukan perbedaan pada tingkat adsorpsi dan desorpsi, begitu juga dengan kristalinitas pada material katalis. Lebih jauh, rasio konten Si/Al juga berubah pada basa dengan konsentrasi terendah. Di sisi lain, tingkat kristalinitas dari katalis mengalami penurunan pada basa dengan konsentrasi tertinggi. Hasil ini diperkuat dengan data FTIR yang menunjukkan perubahan ikatan silanol menjadi silikat dan aluminat. Lebih jauh, analisis morfologi pada katalis menunjukkan bahwa permukaan yang homogen didapatkan dari penggunaan basa dengan konsentrasi rendah. Sebaliknya, basa dengan konsentrasi tinggi memberikan bentuk permukaan katalis yang tidak homogen serta kasar.</dc:description>
	<dc:publisher xml:lang="en">Faculty of Science and Technology Universitas Islam Negeri Ar-Raniry</dc:publisher>
	<dc:date>2020-06-30</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://jurnal.ar-raniry.ac.id/index.php/elkawnie/article/view/6913</dc:identifier>
	<dc:identifier>10.22373/ekw.v6i1.6913</dc:identifier>
	<dc:source xml:lang="en">Elkawnie; Vol. 6 No. 1 (2020); 85-95</dc:source>
	<dc:source>2460-8912</dc:source>
	<dc:source>2460-8920</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://jurnal.ar-raniry.ac.id/index.php/elkawnie/article/view/6913/pdf</dc:relation>
	<dc:relation>https://jurnal.ar-raniry.ac.id/index.php/elkawnie/article/view/6913/10876</dc:relation>
	<dc:rights xml:lang="en">Copyright (c) 2020 Saharman Gea, Agus Haryono, Andriayani Andriayani, Junifa Layla Sihombing, Ahmad Nasir Pulungan, Tiamina Nasution, Rahayu Rahayu, Yasir Arafat Hutapea</dc:rights>
</oai_dc:dc>