Mineralogical, Microstructural and Compressive Strength Characterization of Fly Ash as Materials in Geopolymer Cement

Elkawnie · Vol. 7 No. 1 (2021) · hlm. 1–18

DOI
10.22373/ekw.v7i1.7787
ISSN
2460-8912, 2460-8920
Terbit
2021-07-19
Penerbit
Faculty of Science and Technology Universitas Islam Negeri Ar-Raniry
Bahasa
eng

Abstrak

Abstract: This study was designed to examine the mineral, microstructural, and mechanical strength properties of fly ash and its feasibility as a raw material for geopolymer cement. The study used an experimental method by examining the characteristics of fly ash by X-ray Fluorescence Spectrometer (XRF), Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), hydrometer method, Scanning electron microscopy (SEM), and compressive strength testing. For creating the geopolymer cement paste, a concentration of NaOH 10M was used, with a ratio of water/solid = 0.4 and a ratio of Na2SiO3/NaOH = 1 using curring at room temperature. The results showed the geopolymer pastes have a compressive strength of 18.1 MPa and 21.5 MPa after 7 days and 28 days. The XRD results showed a decrease in the peak of 2θ at 26.54° because the amorphous part had transformed into a C-S-H solution in geopolymer cement. This finding was supported by the FTIR spectra results showing Si-O-Si bending vibration and the functional group of AlO2. It showed that Nagan Raya fly ash-based geopolymer is a potential construction material.Abstrak: Penelitian ini dirancang untuk mendapatkan sifat mineral, mikrostruktural, dan kekuatan mekanis dari fly ash serta kesesuaiannya sebagai material dasar pada semen geopolimer. Metode penelitian yang digunakan adalah metode eksperimen dengan cara menguji karakteristik dari fly ash dengan pengujian X-ray Fluorescense Spectrometer (XRF), Fourier transform infrared (FTIR) spectoscopy, X-ray diffraction (XRD), hydrometer method, Scanning electron microscopy (SEM) dan kuat tekan. Untuk pembuatan pasta semen geopolimer digunakan konsentrasi NaOH 10 M, rasio water/solid 0,4 dan rasio Na2SiO3/NaOH = 1 dengan perawatan pada suhu kamar. Hasil menunjukkan setelah 7 hari pasta geopolimer memiliki kuat tekan 18,1 MPa dan 21,5 MPa pada 28 hari. Hasil XRD menunjukkan adanya penurunan puncak 2θ pada 26,54° ini disebabkan karena bagian amorf dari fly ash telah menjadi larutan C-S-H pada semen geopolimer. Hasil ini diperkuat dengan analisis FTIR spectra yang menunjukkan adanya Si-O-Si bending vibration dan gugus fungsi dari AlO2. Hasil menunjukkan fly ash dari Nagan Raya potensial sebagai bahan material konstruksi berbasis geopolimer.

Kata kunci

Jaringan kolaborasi para penulis

23 penulis · 47 tautan kepenulisan bersama · 18 lintas organisasi

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • Universitas Syiah Kuala
  • Universitas Abulyatama
  • Diponegoro University
  • Bandung Institute of Technology
  • Universitas Iskandar Muda
  • Jiangnan University
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Lia HandayaniUniversitas Abulyatama2
Muttaqin HasanUniversitas Syiah Kuala2
Yuwaldi AwayUniversitas Syiah Kuala1
Fachrurrazi FachrurraziUniversitas Syiah Kuala1
Abdullah AbdullahUniversitas Syiah Kuala1
Ismail ABUniversitas Syiah Kuala1
Edi Syahputra BarusUniversitas Syiah Kuala1
Ichsan SyahputraUniversitas Abulyatama1
Meliyana MeliyanaUniversitas Abulyatama1
Nurhayati NurhayatiUniversitas Abulyatama1
Yayuk AstutiDiponegoro University1
Adi DarmawanDiponegoro University1
Fido YurnalisBandung Institute of Technology1
Li FuJiangnan University1
Zahra AmaliaUniversitas Syiah Kuala1
Nazira Suha Al BakriUniversitas Iskandar Muda1
Reza RizkiUniversitas Syiah Kuala1
Muhammad Prayogie AuliaUniversitas Syiah Kuala1
Farid MulanaUniversitas Syiah Kuala1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://jurnal.ar-raniry.ac.id/index.php/elkawnie/oai, pertama di-harvest 7 Nov 2026, terakhir terlihat 8 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en">Mineralogical, Microstructural and Compressive Strength Characterization of Fly Ash as Materials in Geopolymer Cement</dc:title>
	<dc:creator xml:lang="en">Rahmawati, Cut</dc:creator>
	<dc:creator xml:lang="en">Aprilia, Sri</dc:creator>
	<dc:creator xml:lang="en">Saidi, Taufiq</dc:creator>
	<dc:creator xml:lang="en">Aulia, Teuku Budi</dc:creator>
	<dc:subject xml:lang="en">geopolymer</dc:subject>
	<dc:subject xml:lang="en">fly ash</dc:subject>
	<dc:subject xml:lang="en">epoxy</dc:subject>
	<dc:subject xml:lang="en">cement</dc:subject>
	<dc:subject xml:lang="en">compressive strength</dc:subject>
	<dc:description xml:lang="en">Abstract: This study was designed to examine the mineral, microstructural, and mechanical strength properties of fly ash and its feasibility as a raw material for geopolymer cement. The study used an experimental method by examining the characteristics of fly ash by X-ray Fluorescence Spectrometer (XRF), Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), hydrometer method, Scanning electron microscopy (SEM), and compressive strength testing. For creating the geopolymer cement paste, a concentration of NaOH 10M was used, with a ratio of water/solid = 0.4 and a ratio of Na2SiO3/NaOH = 1 using curring at room temperature. The results showed the geopolymer pastes have a compressive strength of 18.1 MPa and 21.5 MPa after 7 days and 28 days. The XRD results showed a decrease in the peak of 2θ at 26.54° because the amorphous part had transformed into a C-S-H solution in geopolymer cement. This finding was supported by the FTIR spectra results showing Si-O-Si bending vibration and the functional group of AlO2. It showed that Nagan Raya fly ash-based geopolymer is a potential construction material.Abstrak: Penelitian ini dirancang untuk mendapatkan sifat mineral, mikrostruktural, dan kekuatan mekanis dari fly ash serta kesesuaiannya sebagai material dasar pada semen geopolimer. Metode penelitian yang digunakan adalah metode eksperimen dengan cara  menguji karakteristik dari fly ash dengan pengujian X-ray Fluorescense Spectrometer (XRF), Fourier transform infrared (FTIR) spectoscopy, X-ray diffraction (XRD), hydrometer method, Scanning electron microscopy (SEM) dan kuat tekan.  Untuk pembuatan pasta semen geopolimer digunakan konsentrasi NaOH 10 M, rasio water/solid 0,4 dan rasio Na2SiO3/NaOH = 1 dengan perawatan pada suhu kamar. Hasil menunjukkan setelah 7 hari pasta geopolimer memiliki kuat tekan 18,1 MPa dan 21,5 MPa pada 28 hari. Hasil XRD menunjukkan adanya penurunan puncak 2θ pada 26,54° ini disebabkan karena bagian amorf dari fly ash telah menjadi larutan C-S-H pada semen geopolimer. Hasil ini diperkuat dengan analisis FTIR spectra yang menunjukkan adanya Si-O-Si bending vibration dan gugus fungsi dari AlO2. Hasil menunjukkan fly ash dari Nagan Raya potensial sebagai bahan material konstruksi berbasis geopolimer.</dc:description>
	<dc:publisher xml:lang="en">Faculty of Science and Technology Universitas Islam Negeri Ar-Raniry</dc:publisher>
	<dc:date>2021-07-19</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://jurnal.ar-raniry.ac.id/index.php/elkawnie/article/view/7787</dc:identifier>
	<dc:identifier>10.22373/ekw.v7i1.7787</dc:identifier>
	<dc:source xml:lang="en">Elkawnie; Vol. 7 No. 1 (2021); 1-18</dc:source>
	<dc:source>2460-8912</dc:source>
	<dc:source>2460-8920</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://jurnal.ar-raniry.ac.id/index.php/elkawnie/article/view/7787/pdf</dc:relation>
	<dc:rights xml:lang="en">Copyright (c) 2021 Cut Rahmawati, Sri Aprilia, Taufiq Saidi, Teuku Budi Aulia</dc:rights>
</oai_dc:dc>