Adsorption of Cu (II) Heavy Metal From Acid Mine Drainage Using Modified Bentonite With Risk Husk Activated Carbon

Elkawnie · Vol. 9 No. 2 (2023) · hlm. 204–217

DOI
10.22373/ekw.v9i2.16980
ISSN
2460-8912, 2460-8920
Terbit
2023-12-31
Penerbit
Faculty of Science and Technology Universitas Islam Negeri Ar-Raniry
Bahasa
eng

Abstrak

Abstract: Acid mine drainage is a waste product of the mining process that contains several heavy metals, including copper. The purpose of this study was to develop bentonite adsorbent-modified activated carbon from rice husks that will be used to adsorb Cu metal from acid mine drainage. Bentonite was chemically activated with HCl, whereas rice husk was physically and chemically activated in a furnace at 500°C for 2 hours and soaked in HCl. The modification was accomplished by combining activated bentonite and rice husk activated carbon in variations of ratio, which are 1:1, 1:2, 1;3, 1:4, and 1:5. Morphological analysis revealed a surface structure similar to that of coral (sponge). The functional groups identified include the OH, OH2, Al, SiO, SiOAl, and SiOSi functions. The XRD analysis showed a diffractogram at 2θ = 19000o and 20000o that indicates the presence of montmorillonite minerals. The Cu metal adsorption capacity of rice husk-modified bentonite was 3.153 mg/g. The adsorption isotherm obtained in this study is the Freundlich isotherm, with an R2 value of 0.9541. These findings indicate the potential usefulness of the modified adsorbent in mitigating the environmental impact of the industry dealing with acid mine drainage.Abstrak: Air asam tambang merupakan limbah hasil proses penambangan yang mengandung beberapa logam berat, diantaranya tembaga. Tujuan penelitian ini adalah mengembangkan karbon aktif termodifikasi adsorben bentonit dari sekam padi yang akan digunakan untuk mengadsorpsi logam Cu dari air asam tambang. Bentonit diaktivasi secara kimia dengan HCl, sedangkan sekam padi diaktivasi secara fisik dan kimia dengan tanur pada suhu 500°C selama 2 jam dan direndam dalam HCl. Modifikasi dilakukan dengan menggabungkan bentonit aktif dan karbon aktif sekam padi dengan variasi perbandingan 1:1, 1:2, 1;3, 1:4, dan 1:5. Analisis morfologi mengungkapkan struktur permukaan yang mirip dengan karang (spons). Gugus fungsi yang teridentifikasi meliputi fungsi OH, OH2, Al, SiO, SiOAl, dan SiOSi. Analisis XRD menunjukkan difraktogram pada 2θ = 19000o dan 20000o yang menunjukkan adanya mineral montmorillonit. Kapasitas adsorpsi logam Cu pada bentonit termodifikasi sekam padi adalah 3,153 mg/g. Isoterm adsorpsi yang diperoleh pada penelitian ini adalah isoterm Freundlich, dengan nilai R2 sebesar 0,9541. Temuan-temuan ini menunjukkan potensi kegunaan adsorben yang dimodifikasi dalam mengurangi dampak lingkungan bagi industri yang berurusan dengan limbah air tambang asam.

Kata kunci

Jaringan kolaborasi para penulis

40 penulis · 81 tautan kepenulisan bersama · 5 lintas organisasi · menampilkan 40 yang paling banyak terhubung

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • Politeknik Negeri Ujung Pandang
  • Institut Agama Islam Negeri Kendari
  • Universitas Islam Negeri Mahmud Yunus Batusangkar
  • Hasanuddin University
  • Bandung Islamic University
  • Sunan Kalijaga State Islamic University Yogyakarta
  • Afiliasi tidak diketahui
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Pirman PirmanPoliteknik Negeri Ujung Pandang2
Tona Aurora LubisAfiliasi tidak diketahui2
Arifki Budia WarmanUniversitas Islam Negeri Mahmud Yunus Batusangkar2
Zainuddin ZainuddinInstitut Agama Islam Negeri Kendari2
Rozi AndriniAfiliasi tidak diketahui2
Muhammad YanisAfiliasi tidak diketahui2
Syafaruddin SyafaruddinHasanuddin University1
La Ode SuriadiAfiliasi tidak diketahui1
Ambo Wonua NusantaraAfiliasi tidak diketahui1
Heppi MilliaAfiliasi tidak diketahui1
M. NatsirAfiliasi tidak diketahui1
Pasrun AdamAfiliasi tidak diketahui1
Reza Nur WahidAfiliasi tidak diketahui1
Abdul RohmanBandung Islamic University1
Wasehudin WasehudinAfiliasi tidak diketahui1
Muh Barid Nizarudin WajdiAfiliasi tidak diketahui1
EDWIN BUSTAMIAfiliasi tidak diketahui1
SYAMSURIZAL TANAfiliasi tidak diketahui1
Tri Supryjadi LiuAfiliasi tidak diketahui1
Tasya TiarifaniAfiliasi tidak diketahui1
Nurliana NurlianaAfiliasi tidak diketahui1
Sugito SugitoAfiliasi tidak diketahui1
Devi MegawatiAfiliasi tidak diketahui1
Ainul MardhiahAfiliasi tidak diketahui1
Badrul MunirAfiliasi tidak diketahui1
Syafrizal IdrisAfiliasi tidak diketahui1
Dian DarismaAfiliasi tidak diketahui1
Rifa Salma SalsabilaAfiliasi tidak diketahui1
Kusmawati HattaAfiliasi tidak diketahui1
Shahira UlfaAfiliasi tidak diketahui1
Nurul FajarAfiliasi tidak diketahui1
Nursa'di IbrahimAfiliasi tidak diketahui1
Saifuddin Zuhri QudsySunan Kalijaga State Islamic University Yogyakarta1
Novita CahyaniAfiliasi tidak diketahui1
Kemas Muhammad GemilangAfiliasi tidak diketahui1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://jurnal.ar-raniry.ac.id/index.php/elkawnie/oai, pertama di-harvest 7 Nov 2026, terakhir terlihat 8 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en">Adsorption of Cu (II) Heavy Metal From Acid Mine Drainage Using Modified Bentonite With Risk Husk Activated Carbon</dc:title>
	<dc:creator xml:lang="en">Zulkifli, Zulkifli</dc:creator>
	<dc:creator xml:lang="en">Marwan, Marwan</dc:creator>
	<dc:creator xml:lang="en">Meurah Rosnelly, Cut</dc:creator>
	<dc:creator xml:lang="en">Munawar, Edi</dc:creator>
	<dc:creator xml:lang="en">Meilina, Hesti</dc:creator>
	<dc:subject xml:lang="en">Acid mine drainage</dc:subject>
	<dc:subject xml:lang="en">Adsorption</dc:subject>
	<dc:subject xml:lang="en">Bentonite</dc:subject>
	<dc:description xml:lang="en">Abstract: Acid mine drainage is a waste product of the mining process that contains several heavy metals, including copper. The purpose of this study was to develop bentonite adsorbent-modified activated carbon from rice husks that will be used to adsorb Cu metal from acid mine drainage. Bentonite was chemically activated with HCl, whereas rice husk was physically and chemically activated in a furnace at 500°C for 2 hours and soaked in HCl. The modification was accomplished by combining activated bentonite and rice husk activated carbon in variations of ratio, which are 1:1, 1:2, 1;3, 1:4, and 1:5. Morphological analysis revealed a surface structure similar to that of coral (sponge). The functional groups identified include the OH, OH2, Al, SiO, SiOAl, and SiOSi functions. The XRD analysis showed a diffractogram at 2θ = 19000o and 20000o that indicates the presence of montmorillonite minerals. The Cu metal adsorption capacity of rice husk-modified bentonite was 3.153 mg/g. The adsorption isotherm obtained in this study is the Freundlich isotherm, with an R2 value of 0.9541. These findings indicate the potential usefulness of the modified adsorbent in mitigating the environmental impact of the industry dealing with acid mine drainage.Abstrak: Air asam tambang merupakan limbah hasil proses penambangan yang mengandung beberapa logam berat, diantaranya tembaga. Tujuan penelitian ini adalah mengembangkan karbon aktif termodifikasi adsorben bentonit dari sekam padi yang akan digunakan untuk mengadsorpsi logam Cu dari air asam tambang. Bentonit diaktivasi secara kimia dengan HCl, sedangkan sekam padi diaktivasi secara fisik dan kimia dengan tanur pada suhu 500°C selama 2 jam dan direndam dalam HCl. Modifikasi dilakukan dengan menggabungkan bentonit aktif dan karbon aktif sekam padi dengan variasi perbandingan 1:1, 1:2, 1;3, 1:4, dan 1:5. Analisis morfologi mengungkapkan struktur permukaan yang mirip dengan karang (spons). Gugus fungsi yang teridentifikasi meliputi fungsi OH, OH2, Al, SiO, SiOAl, dan SiOSi. Analisis XRD menunjukkan difraktogram pada 2θ = 19000o dan 20000o yang menunjukkan adanya mineral montmorillonit. Kapasitas adsorpsi logam Cu pada bentonit termodifikasi sekam padi adalah 3,153 mg/g. Isoterm adsorpsi yang diperoleh pada penelitian ini adalah isoterm Freundlich, dengan nilai R2 sebesar 0,9541. Temuan-temuan ini menunjukkan potensi kegunaan adsorben yang dimodifikasi dalam mengurangi dampak lingkungan bagi industri yang berurusan dengan limbah air tambang asam.</dc:description>
	<dc:publisher xml:lang="en">Faculty of Science and Technology Universitas Islam Negeri Ar-Raniry</dc:publisher>
	<dc:date>2023-12-31</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://jurnal.ar-raniry.ac.id/index.php/elkawnie/article/view/16980</dc:identifier>
	<dc:identifier>10.22373/ekw.v9i2.16980</dc:identifier>
	<dc:source xml:lang="en">Elkawnie; Vol. 9 No. 2 (2023); 204-217</dc:source>
	<dc:source>2460-8912</dc:source>
	<dc:source>2460-8920</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://jurnal.ar-raniry.ac.id/index.php/elkawnie/article/view/16980/pdf</dc:relation>
	<dc:rights xml:lang="en">Copyright (c) 2023 Zulkifli Zulkifli, Marwan Marwan, Cut Meurah Rosnelly, Edi Munawar, Hesti Meilina</dc:rights>
</oai_dc:dc>