Effectiveness of bleaching agent on composite resin discoloration

Dental Journal (Majalah Kedokteran Gigi) · Vol. 45 No. 1 (2012) · hlm. 43–47

DOI
10.20473/j.djmkg.v45.i1.p43-47
ISSN
2442-9740, 1978-3728
Terbit
2012-03-01
Penerbit
Faculty of Dental Medicine, Universitas Airlangga https://fkg.unair.ac.id/en
Bahasa
eng

Abstrak

Background: The discoloration of teeth, especially anterior teeth, is one of aesthetic problems. The use of tooth bleaching agents for discolored natural teeth is becoming increasingly popular. Many dentists, however, get many problems when they conduct bleaching process since there is much composite filling on patient's anterior teeth. Although many research have focused on the discoloration of composite resin after bleaching process, the problem still becomes debatable. Purpose: The purpose of this study was to investigate the difference of the discoloration between hybrid composite and nano composite before and after the application of tooth bleaching agent, 38% hydrogen peroxide. Methods: Eighteen disk-shaped specimens (5 mm) of each of two composite resins, hybrid and nano filler, were prepared. The each group was treated 3 times and the specimens were divided into two groups consisted of 9 specimens for each, and then immersed in black tea solutions for 72 hours. Next, after having staining and bleaching processes, the color of the specimens was measured with a optic spectrophotometer by using photo with type BPY-47 and digital microvolt. The differences of the light intensity among three measurements were then calculated. Afterwards, GLM MANOVA Repeated Measure and parametric analysis (Independent t-test and Paired t-test) were then used to analyze the data. Results: After staining process, it is then known that the nano composite had more discoloration and more affected by the black tea solution than the hybrid one. Conclusion: After bleaching, the discoloration was finally removed completely from both hybride and nano filler composite resins and became brighter from the baseline color.Latar belakang: Salah satu problem estetik adalah adanya perubahan warna pada gigi anterior. Peningkatan pemakaian bahan bleaching semakin popular. Banyak dokter gigi mempunyai problem ketika mereka akan melakukan proses bleaching dan ditemukan banyak tumpatan komposit pada gigi anteriornya. Meskipun telah banyak penelitiahan yang dilakukan tetapi masalah ini masih menjadi pro dan kontra. Tujuan: Melihat perbedaan perubahan warna antara komposit hybrid dan komposit nano sebelum dan sesudah terpapar bahan pemutih gigi hidrogen peroksida 38%. Metode: Tiap kelompok mendapatkan perlakuan 3 kali. Dipersiapka 18 spesimen berbentuk tabung (5 mm) dan dibagi menjadi 2 kelompok masing-masing 9 untuk resin komposite hybrid dan komposit nano. Direndam larutan teh hitam selama 72 jam. Perubahan warna diukur dengan spektrofotometer tipe BPY-47 dan mikrovolt digital, baik sebelum, setelah perendaman larutan teh hitam dan setelah proses bleaching. Perbedaan intensitas cahaya dihitung dengan GLM MANOVA Repeated Measuse dan analisa parametrik. Hasil: Setelah perendaman teh hitam, komposit nano mempunyai perubahan warna yang lebih gelap dibandingkan komposit hybrid. Setelah bleaching, baik komposite hybrid dan komposit nano kembali ke warna aslinya. Tetapi perubahan warna komposit nano lebih besar dari pada komposit hybrid. Kesimpulan: Setelah bleaching, baik resin komposit hybrid dan nano menjadi lebih terang dari warna aslinya.

Kata kunci

Jaringan kolaborasi para penulis

13 penulis · 42 tautan kepenulisan bersama

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • Afiliasi tidak diketahui
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Nirawati PribadiAfiliasi tidak diketahui1
Hendy Jaya KurniawanAfiliasi tidak diketahui1
S. SukatonAfiliasi tidak diketahui1
S. SylviaAfiliasi tidak diketahui1
Maya SafitriAfiliasi tidak diketahui1
Rahmadanty MustikaAfiliasi tidak diketahui1
Ananta Tantri BudiAfiliasi tidak diketahui1
Eric Priyo PrasetyoAfiliasi tidak diketahui1
Devi Eka JuniartiAfiliasi tidak diketahui1
Dian Agustin WahjuningrumAfiliasi tidak diketahui1
Dyanita HasriAfiliasi tidak diketahui1
Evelyn TjendronegoroAfiliasi tidak diketahui1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://e-journal.unair.ac.id/MKG/oai, pertama di-harvest 8 Nov 2026, terakhir terlihat 8 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en-US">Effectiveness of bleaching agent on composite resin discoloration</dc:title>
	<dc:creator>Sampoerno, Galih</dc:creator>
	<dc:subject xml:lang="en-US">Discoloration</dc:subject>
	<dc:subject xml:lang="en-US">composite resins</dc:subject>
	<dc:subject xml:lang="en-US">bleaching agent</dc:subject>
	<dc:subject xml:lang="en-US">Perubahan warna</dc:subject>
	<dc:subject xml:lang="en-US">resin komposit</dc:subject>
	<dc:subject xml:lang="en-US">bahan bleaching</dc:subject>
	<dc:description xml:lang="en-US">Background: The discoloration of teeth, especially anterior teeth, is one of aesthetic problems. The use of tooth bleaching agents for discolored natural teeth is becoming increasingly popular. Many dentists, however, get many problems when they conduct bleaching process since there is much composite filling on patient's anterior teeth. Although many research have focused on the discoloration of composite resin after bleaching process, the problem still becomes debatable. Purpose: The purpose of this study was to investigate the difference of the discoloration between hybrid composite and nano composite before and after the application of tooth bleaching agent, 38% hydrogen peroxide. Methods: Eighteen disk-shaped specimens (5 mm) of each of two composite resins, hybrid and nano filler, were prepared. The each group was treated 3 times and the specimens were divided into two groups consisted of 9 specimens for each, and then immersed in black tea solutions for 72 hours. Next, after having staining and bleaching processes, the color of the specimens was measured with a optic spectrophotometer by using photo with type BPY-47 and digital microvolt. The differences of the light intensity among three measurements were then calculated. Afterwards, GLM MANOVA Repeated Measure and parametric analysis (Independent t-test and Paired t-test) were then used to analyze the data. Results: After staining process, it is then known that the nano composite had more discoloration and more affected by the black tea solution than the hybrid one. Conclusion: After bleaching, the discoloration was finally removed completely from both hybride and nano filler composite resins and became brighter from the baseline color.Latar belakang: Salah satu problem estetik adalah adanya perubahan warna pada gigi anterior. Peningkatan pemakaian bahan bleaching semakin popular. Banyak dokter gigi mempunyai problem ketika mereka akan melakukan proses bleaching dan ditemukan banyak tumpatan komposit pada gigi anteriornya. Meskipun telah banyak penelitiahan yang dilakukan tetapi masalah ini masih menjadi pro dan kontra. Tujuan: Melihat perbedaan perubahan warna antara komposit hybrid dan komposit nano sebelum dan sesudah terpapar bahan pemutih gigi hidrogen peroksida 38%. Metode: Tiap kelompok mendapatkan perlakuan 3 kali. Dipersiapka 18 spesimen berbentuk tabung (5 mm) dan dibagi menjadi 2 kelompok masing-masing 9 untuk resin komposite hybrid dan komposit nano. Direndam larutan teh hitam selama 72 jam. Perubahan warna diukur dengan spektrofotometer tipe BPY-47 dan mikrovolt digital, baik sebelum, setelah perendaman larutan teh hitam dan setelah proses bleaching. Perbedaan intensitas cahaya dihitung dengan GLM MANOVA Repeated Measuse dan analisa parametrik. Hasil: Setelah perendaman teh hitam, komposit nano mempunyai perubahan warna yang lebih gelap dibandingkan komposit hybrid. Setelah bleaching, baik komposite hybrid dan komposit nano kembali ke warna aslinya. Tetapi perubahan warna komposit nano lebih besar dari pada komposit hybrid. Kesimpulan: Setelah bleaching, baik resin komposit hybrid dan nano menjadi lebih terang dari warna aslinya.</dc:description>
	<dc:publisher xml:lang="en-US">Faculty of Dental Medicine, Universitas Airlangga https://fkg.unair.ac.id/en</dc:publisher>
	<dc:date>2012-03-01</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en-US">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://e-journal.unair.ac.id/MKG/article/view/843</dc:identifier>
	<dc:identifier>10.20473/j.djmkg.v45.i1.p43-47</dc:identifier>
	<dc:source xml:lang="en-US">Dental Journal (Majalah Kedokteran Gigi); Vol. 45 No. 1 (2012): March 2012; 43-47</dc:source>
	<dc:source>2442-9740</dc:source>
	<dc:source>1978-3728</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://e-journal.unair.ac.id/MKG/article/view/843/626</dc:relation>
	<dc:rights xml:lang="en-US">Copyright (c) 2015 Dental Journal (Majalah Kedokteran Gigi)</dc:rights>
</oai_dc:dc>