Pembuatan Ba0,8Sr0,2TiO3 menggunakan Metode Co-precipitation dengan Variasi Suhu Sintering

INDONESIAN JOURNAL OF APPLIED PHYSICS · Vol. 7 No. 1 (2017) · hlm. 52–58

DOI
10.13057/ijap.v7i1.1776
ISSN
2477-6416, 2089-0133
Terbit
2017-08-08
Penerbit
Department of Physics, Sebelas Maret University
Bahasa
eng

Abstrak

Ba0,8Sr0,2TiO3 was made by co-precipitation method with the sintering temperature of 600oC, 700oC, 800oC and 900oC for 4 hours. Sintering temperature was varied to investigate its effect on microstructure and dielectric constant of Ba0,8Sr0,2TiO3. microstructure characterization was performed by X-Ray Diffraction (XRD) instrument. Dielectric constant characterization was perform by LCR meter. The crystal size increased significantly with increasing sintering temperature. Measurements of dielectric constant were performed at range of frequency 0.01 to 100 KHz. Dielectric constant value is highest at the lowest frequency. Dielectric constant value size increased significantly with increasing sintering temperature.

Jaringan kolaborasi para penulis

37 penulis · 123 tautan kepenulisan bersama · 3 lintas organisasi

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • Sebelas Maret University
  • Cenderawasih University
  • IAIN Kudus
  • National Research and Innovation Agency
  • Afiliasi tidak diketahui
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Risa SuryanaSebelas Maret University4
Agus SupriyantoIAIN Kudus3
Nurdiyantoro Putra PrasetyaAfiliasi tidak diketahui2
Sistha Ridha AlfidharistiAfiliasi tidak diketahui2
Novinda Hary MegasariAfiliasi tidak diketahui2
Desita Suci PangestiAfiliasi tidak diketahui2
Rachmat HidayatNational Research and Innovation Agency1
Devara Ega FaustaAfiliasi tidak diketahui1
Ahmad MarzukiAfiliasi tidak diketahui1
Saidatul NisyaAfiliasi tidak diketahui1
Kharenina Zalfa' ShalihahAfiliasi tidak diketahui1
Parahita FaqihAfiliasi tidak diketahui1
Zulaldi Yahya DewanggaAfiliasi tidak diketahui1
Nadya Aruma DewiAfiliasi tidak diketahui1
Dianisa Khoirum SandiAfiliasi tidak diketahui1
Anif JamaludinAfiliasi tidak diketahui1
Suharno SuharnoCenderawasih University1
Nuryani NuryaniAfiliasi tidak diketahui1
Budi PurnamaAfiliasi tidak diketahui1
Utari UtariAfiliasi tidak diketahui1
Riyatun RiyatunAfiliasi tidak diketahui1
Ramadona RahmawatiAfiliasi tidak diketahui1
Adiana MusadewiAfiliasi tidak diketahui1
Sri BudiawantiAfiliasi tidak diketahui1
Dwi Teguh RahardjoAfiliasi tidak diketahui1
Husnah RofikoAfiliasi tidak diketahui1
Novi Dyah PuspitasariAfiliasi tidak diketahui1
Untung RiyadiAfiliasi tidak diketahui1
Sophia Dewi Nur AnisaAfiliasi tidak diketahui1
Kusumandari KusumandariAfiliasi tidak diketahui1
Zakaria Sandy PamungkasAfiliasi tidak diketahui1
Nonoh Siti AminahAfiliasi tidak diketahui1
Widha SunarnoSebelas Maret University1
Maura Trynovita SakliressyCenderawasih University1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://jurnal.uns.ac.id/ijap/oai, pertama di-harvest 8 Nov 2026, terakhir terlihat 8 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en-US">Pembuatan Ba0,8Sr0,2TiO3 menggunakan Metode Co-precipitation dengan Variasi Suhu Sintering</dc:title>
	<dc:creator>Nita, Isma Alvia</dc:creator>
	<dc:creator>Iriani, Yofentina</dc:creator>
	<dc:creator>Nurosyid, Fahru</dc:creator>
	<dc:description xml:lang="en-US">Ba0,8Sr0,2TiO3 was made by co-precipitation method with the sintering temperature of 600oC, 700oC, 800oC and 900oC for 4 hours. Sintering temperature was varied to investigate its effect on microstructure and dielectric constant of Ba0,8Sr0,2TiO3. microstructure characterization was performed by X-Ray Diffraction (XRD) instrument. Dielectric constant characterization was perform by LCR meter. The crystal size increased significantly with increasing sintering temperature. Measurements of dielectric constant were performed at range of frequency 0.01 to 100 KHz. Dielectric constant value is highest at the lowest frequency. Dielectric constant value size increased significantly with increasing sintering temperature.</dc:description>
	<dc:publisher xml:lang="en-US">Department of Physics, Sebelas Maret University</dc:publisher>
	<dc:contributor xml:lang="en-US"></dc:contributor>
	<dc:date>2017-08-08</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en-US">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://jurnal.uns.ac.id/ijap/article/view/1776</dc:identifier>
	<dc:identifier>10.13057/ijap.v7i1.1776</dc:identifier>
	<dc:source xml:lang="en-US">INDONESIAN JOURNAL OF APPLIED PHYSICS; Vol 7, No 1 (2017): April; 52-58</dc:source>
	<dc:source>2477-6416</dc:source>
	<dc:source>2089-0133</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://jurnal.uns.ac.id/ijap/article/view/1776/11078</dc:relation>
	<dc:rights xml:lang="en-US">Copyright (c) 2017 INDONESIAN JOURNAL OF APPLIED PHYSICS</dc:rights>
</oai_dc:dc>