Structural Investigation and Properties Of Tio2 Thin Film Prepared by Sol-Gel Spin Coating

INDONESIAN JOURNAL OF APPLIED PHYSICS · Vol. 12 No. 2 (2022) · hlm. 251–257

DOI
10.13057/ijap.v12i2.59567
ISSN
2477-6416, 2089-0133
Terbit
2022-10-04
Penerbit
Department of Physics, Sebelas Maret University
Bahasa
eng

Abstrak

We report the structural properties of TiO2 (Titanium dioxide) thin films grown using sol-gel spin coating method for temperature treatment (with temperature 50o C and without temperature) The difference in temperature is carried out to determine changes in the surface of the sample by using heating or not. Ideally, the thickness of the TiO2 layer ranges from 10-15 μm, therefore in this study it was carried out in 5 layers. Field Emission Scanning Electron Microscopy (FESEM) consist of surface morphology, Cross-section sample, and EDX images, respectively, providing the structure of the surface. The result confirm that temperature treatment can damage the surface coating, this is proven by the shape of the crack in the coating.

Kata kunci

Jaringan kolaborasi para penulis

40 penulis · 193 tautan kepenulisan bersama · menampilkan 40 yang paling banyak terhubung

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • Politeknik Negeri Ujung Pandang
  • National Research and Innovation Agency
  • Afiliasi tidak diketahui
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Ari Handono RamelanAfiliasi tidak diketahui3
Fahru NurosyidAfiliasi tidak diketahui2
Fatimah FatimahAfiliasi tidak diketahui2
Prima Suci RohmadhenyAfiliasi tidak diketahui2
Trikinasih HandayaniAfiliasi tidak diketahui2
Wahyu Nanda Eka SaputraAfiliasi tidak diketahui2
M. Arif HakimAfiliasi tidak diketahui1
Rachmat HidayatNational Research and Innovation Agency1
Devara Ega FaustaAfiliasi tidak diketahui1
Ahmad MarzukiAfiliasi tidak diketahui1
Saidatul NisyaAfiliasi tidak diketahui1
Kharenina Zalfa' ShalihahAfiliasi tidak diketahui1
Ni'matuzahroh Ni'matuzahrohAfiliasi tidak diketahui1
Farah Aisyah NafidiastriAfiliasi tidak diketahui1
Salamun SalamunAfiliasi tidak diketahui1
Tri NurhariyatiAfiliasi tidak diketahui1
Izdihar TsanaAfiliasi tidak diketahui1
Nurhayati NurhayatiPoliteknik Negeri Ujung Pandang1
nurjanah nurjanahAfiliasi tidak diketahui1
Sihono SihonoAfiliasi tidak diketahui1
Bagus Sediadi Bandol UtomoAfiliasi tidak diketahui1
Subaryono SubaryonoAfiliasi tidak diketahui1
Wahyu RamadhanAfiliasi tidak diketahui1
Ellya SinuratAfiliasi tidak diketahui1
Fateha FatehaAfiliasi tidak diketahui1
Theresia Dwi SuryaningrumAfiliasi tidak diketahui1
Dina FransiskaAfiliasi tidak diketahui1
Bakti Berlyanto SedayuAfiliasi tidak diketahui1
Waryanto WaryantoAfiliasi tidak diketahui1
Hafidz Maulana FadillahAfiliasi tidak diketahui1
Alief Laily MuzayyanahAfiliasi tidak diketahui1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://jurnal.uns.ac.id/ijap/oai, pertama di-harvest 8 Nov 2026, terakhir terlihat 8 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en-US">Structural Investigation and Properties Of Tio2 Thin Film Prepared by Sol-Gel Spin Coating</dc:title>
	<dc:creator>Saputri, Diani Galih</dc:creator>
	<dc:creator>Bin Ahmad, Mohd Khairul</dc:creator>
	<dc:creator>Supriyanto, Agus</dc:creator>
	<dc:creator>Nasyori, Achmad</dc:creator>
	<dc:creator>Kunya, Salisu I</dc:creator>
	<dc:creator>Maarof, Nurul Amiera Shahida</dc:creator>
	<dc:creator>Abd Majid, Siti Nurhaziqah</dc:creator>
	<dc:creator>Mohd Ismail, Anis Zafirah</dc:creator>
	<dc:creator>Ahmad Ramli, Shazleen</dc:creator>
	<dc:subject xml:lang="en-US">DSSC; morphology; spin coating; TiO2</dc:subject>
	<dc:description xml:lang="en-US">We report the structural properties of TiO2 (Titanium dioxide) thin films grown using sol-gel spin coating method for temperature treatment (with temperature 50o C and without temperature) The difference in temperature is carried out to determine changes in the surface of the sample by using heating or not. Ideally, the thickness of the TiO2 layer ranges from 10-15 μm, therefore in this study it was carried out in 5 layers. Field Emission Scanning Electron Microscopy (FESEM) consist of surface morphology, Cross-section sample, and EDX images, respectively, providing the structure of the surface. The result confirm that temperature treatment can damage the surface coating, this is proven by the shape of the crack in the coating.</dc:description>
	<dc:publisher xml:lang="en-US">Department of Physics, Sebelas Maret University</dc:publisher>
	<dc:contributor xml:lang="en-US"></dc:contributor>
	<dc:date>2022-10-04</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en-US">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://jurnal.uns.ac.id/ijap/article/view/59567</dc:identifier>
	<dc:identifier>10.13057/ijap.v12i2.59567</dc:identifier>
	<dc:source xml:lang="en-US">INDONESIAN JOURNAL OF APPLIED PHYSICS; Vol 12, No 2 (2022): October; 251-257</dc:source>
	<dc:source>2477-6416</dc:source>
	<dc:source>2089-0133</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://jurnal.uns.ac.id/ijap/article/view/59567/37678</dc:relation>
</oai_dc:dc>