PENGARUH PENAMBAHAN FLY ASH PADA CAMPURAN BETON DENGAN STEAM CURING 80ºC MENGGUNAKAN SEMEN TIPE 1 (OPC)

Media Konstruksi : Jurnal Ilmiah Teknik Sipil · Vol. 4 No. 2 (2019)

DOI
10.33772/jmk.v4i2.27219
ISSN
2503-2712
Published
2019-07-01
Publisher
PRODI D3 TEKNIK SIPIL
Language
eng

Abstract

Abstract The purpose of this study was to determine the compressive strength of concrete by using fly ash as a material for reducing the need for cement in mixed variations of 0%, 5%, 10%, 15%, 20%, 25%, 30% with a treatment temperature of 80̊C for 1 day.This test is a research study in the laboratory by examining fine aggregates and coarse aggregates. In this study the composition of the mixture that will be used is contained in the mix desing analysis with variations of the mixture of fly ash 0%, 5%, 10%, 15%, 20%, 25%, 30% with a maintenance temperature of 80ºC for 24 hours later at soak using ordinary water for 28 days using the SNI method.The value of concrete compressive strength on average at the age of 3 days using maintenance temperature of 80ºC for 24 hours occurred at 0% variation of 23.27 MPa, the value of 7-day concrete compressive strength occurred at 0% variation of 23.93 and the compressive strength value 28 days old concrete occurs in a variation of 0% of 32.56. Abstrak Tujuan dari penelitian ini adalah untuk mengetahui kuat tekan beton dengan menggunakan fly ash sebagai bahan pengurangan kebutuhan semen pada variasi campurn 0%, 5%, 10%, 15%, 20%, 25%, 30% dengan perawatan suhu 80̊C selama 1 hari.Pengujian ini merupakan studi penelitian di laboratorium dengan melakukan pemeriksaan agregat halus dan agregat kasar. Pada peneltian ini komposisi campuran yang akan di gunakan yaitu terdapat dalam analisa mix desing dengan variasi campuran fly ash 0%,5%, 10%, 15%, 20%, 25%, 30% dengan perawatan suhu 80ºC c selama 24 jam kemudian di rendam menggunakan air biasa selama umur 28 hari menggunakan metode SNI.Nilai kuat tekan beton rata – rata pada umur 3 hari dengan menggunakan perawatan suhu 80ºC selama 24 jam terjadi pada variasi 0% sebesar 23,27 Mpa, nilai kuat tekan beton umur 7 hari terjadi pada variasi 0% sebesar 23,93 dan nilai kuat tekan beton umur 28 hari terjadi pada variasi 0% sebesar 32,56.

Collaboration network of the authors

26 authors · 56 co-authorship links · 3 across different organisations

Hover or tap a name to highlight its co-authors. Double-click to open the author's page.

  • Universitas Halu Oleo
  • Universitas Sulawesi Tenggara
  • Affiliation unknown
  • Different organisations
  • Same organisation
  • Affiliation unknown
  • Thicker line = more joint articles · bigger circle = more articles
Show as table
Co-authorOrganisationJoint articles
Wayan MustikaAffiliation unknown3
sulha sulhaAffiliation unknown3
Fitriah Mas'udAffiliation unknown2
I Komang Arya Yogi ParamitaAffiliation unknown2
Riyan Abdillah TakdirUniversitas Halu Oleo1
Adris Ade PutraUniversitas Halu Oleo1
Abdi Juryan LadiantoUniversitas Halu Oleo1
Irwan LakawaUniversitas Sulawesi Tenggara1
Laode Muhammad Fahrizal AhsanUniversitas Sulawesi Tenggara1
Muzammil MakmurUniversitas Sulawesi Tenggara1
Randa PratamaUniversitas Sulawesi Tenggara1
Juprianto JupriantoAffiliation unknown1
Aloysius A. Prima MangiriAffiliation unknown1
Ferdinal FerdinalAffiliation unknown1
Awilliambuth LewikintaAffiliation unknown1
Elkris Vebriana SaleppangAffiliation unknown1
Susi KarmilaAffiliation unknown1
Fahril AlwanAffiliation unknown1
Irvan JayaAffiliation unknown1
Lucky LuckyAffiliation unknown1
Siti Nurjanah AhmadUniversitas Halu Oleo1
Muh Thahir AzikinAffiliation unknown1
RIdwansyah NuhunAffiliation unknown1

Affiliations come from OpenAlex; journal OAI-PMH metadata carries none. Authors without an OpenAlex ID are matched by name, which can merge or split people.

Metadata source: OAI-PMH (metadata jurnal) https://ojs.uho.ac.id/index.php/MedKons/oai, first harvested 31 Okt 2026, last seen 31 Okt 2026.
Original metadata (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en-US">PENGARUH PENAMBAHAN FLY ASH PADA CAMPURAN BETON DENGAN STEAM CURING 80ºC MENGGUNAKAN SEMEN TIPE 1 (OPC)</dc:title>
	<dc:creator>Mangiri, Raymond N.</dc:creator>
	<dc:creator>Tamburaka, Romy S. E.</dc:creator>
	<dc:creator>Makmur, Muammar</dc:creator>
	<dc:description xml:lang="en-US"> Abstract The purpose of this study was to determine the compressive strength of concrete by using fly ash as a material for reducing the need for cement in mixed variations of 0%, 5%, 10%, 15%, 20%, 25%, 30% with a treatment temperature of 80̊C for 1 day.This test is a research study in the laboratory by examining fine aggregates and coarse aggregates. In this study the composition of the mixture that will be used is contained in the mix desing analysis with variations of the mixture of fly ash 0%, 5%, 10%, 15%, 20%, 25%, 30% with a maintenance temperature of 80ºC for 24 hours later at soak using ordinary water for 28 days using the SNI method.The value of concrete compressive strength on average at the age of 3 days using maintenance temperature of 80ºC for 24 hours occurred at 0% variation of 23.27 MPa, the value of 7-day concrete compressive strength occurred at 0% variation of 23.93 and the compressive strength value 28 days old concrete occurs in a variation of 0% of 32.56.  Abstrak Tujuan dari penelitian ini adalah untuk mengetahui kuat tekan beton dengan menggunakan fly ash sebagai bahan pengurangan kebutuhan semen pada variasi campurn 0%, 5%, 10%, 15%, 20%, 25%, 30% dengan perawatan suhu 80̊C selama 1 hari.Pengujian ini merupakan studi penelitian di laboratorium dengan melakukan pemeriksaan agregat halus dan agregat kasar. Pada peneltian ini komposisi campuran yang akan di gunakan yaitu terdapat dalam analisa mix desing dengan variasi campuran fly ash 0%,5%, 10%, 15%, 20%, 25%, 30% dengan perawatan suhu 80ºC c selama 24 jam kemudian di rendam menggunakan air biasa selama umur 28 hari menggunakan metode SNI.Nilai kuat tekan beton rata – rata pada umur 3 hari dengan menggunakan perawatan suhu 80ºC selama 24 jam terjadi pada variasi 0% sebesar 23,27 Mpa, nilai kuat tekan beton umur 7 hari terjadi pada variasi 0% sebesar 23,93 dan nilai kuat tekan beton umur 28 hari terjadi pada variasi 0% sebesar 32,56. </dc:description>
	<dc:publisher xml:lang="en-US">PRODI D3 TEKNIK SIPIL</dc:publisher>
	<dc:contributor xml:lang="en-US"></dc:contributor>
	<dc:date>2019-07-01</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en-US">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://ojs.uho.ac.id/index.php/MedKons/article/view/27219</dc:identifier>
	<dc:identifier>10.33772/jmk.v4i2.27219</dc:identifier>
	<dc:source xml:lang="en-US">Media Konstruksi : Jurnal Ilmiah Teknik Sipil; Vol 4, No 2 (2019): MedKons</dc:source>
	<dc:source>2503-2712</dc:source>
	<dc:source>10.33772/jmk.v4i2</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://ojs.uho.ac.id/index.php/MedKons/article/view/27219/15864</dc:relation>
	<dc:rights xml:lang="en-US">Copyright (c) 2022 MEDIA KONSTRUKSI</dc:rights>
</oai_dc:dc>