The Improvement of Jabon Wood Density Through The Furfuryl Alcohol and Nano-SiO2: Pengingkatan Kerapatan Kayu Jabon Melalui Impregnasi Furfuril Alkohol dan Nano-SiO2

Pengingkatan Kerapatan Kayu Jabon Melalui Impregnasi Furfuril Alkohol dan Nano-SiO2: The Improvement of Jabon Wood Density Through The Furfuryl Alcohol and Nano-SiO2

PERENNIAL · Vol. 21 No. 1 (2025) · hlm. 24–29

DOI
10.24259/perennial.v21i1.43187
ISSN
2685-6859, 1412-7784
Terbit
2025-04-30
Penerbit
Forestry Faculty of Hasanuddin University
Bahasa
en

Abstrak

Inggris

Jabon (Anthocephalus cadamba Miq.) is a fast-growing wood that is widely utilized by the society as a construction material and furniture making. This study aimed to increase the density of jabon wood through a vacuum pressure impregnation method. Furfuryl alcohol (FA) and nano-SiO2 with three concentrations (0.5%, 0.75%, dan 1%) were used as impregnation additives, with control and FA without nanoparticles as comparisons. Impregnation was initiated with a vacuum (0.5 bar) for an hour, followed by pressure (2.5 bar) for 2 hours. The significant results on the physical properties of jabon wood including weight percent gain (WPG), bulking effect (BE), and density showed the success of the modification treatment through the FA and nano-SiO2 impregnation process with various concentrations, which the wood density increased from 0.60 g/cm3 to 0.94 g/cm3. The composition of FA and 1% nano-SiO2 solution was the best treatment to obtain the highest density in modified jabon wood.

Bahasa Indonesia

Kayu jabon (Anthocephalus cadamba Miq.) merupakan kayu cepat tumbuh yang banyak diminati masyarakat untuk dimanfaatkan sebagai bahan konstruksi dan pembuatan furnitur. Penelitian ini bertujuan untuk meningkatkan kerapatan kayu jabon melalui metode impregnasi vakum tekan. Furfuril alkohol (FA) dan nano-SiO2 dengan tiga konsentrasi (0.5%, 0.75%, dan 1%) digunakan sebagai bahan impregnan, dengan kontrol dan perlakuan FA tanpa nanopartikel sebagai pembanding. Impregnasi dimulai dengan pemberian vakum (0.5 bar) selama 1 jam, dilanjutkan dengan tekan (2.5 bar) selama 2 jam. Hasil yang signifikan pada sifat fisis kayu jabon yang meliputi weight percent gain (WPG), bulking effect (BE), dan kerapatan menunjukkan keberhasilan perlakuan modifikasi melalui proses impregnasi FA dan nano-SiO2 dengan berbagai konsentrasi, yang mana kerapatan kayu meningkat dari 0.60 g/cm3 menjadi 0.94 g/cm3. Komposisi larutan FA dan nano-SiO2 1% menjadi perlakuan terbaik untuk mendapatkan nilai kerapatan tertinggi pada kayu jabon termodifikasi.

Kata kunci

Jaringan kolaborasi para penulis

16 penulis · 84 tautan kepenulisan bersama

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • Afiliasi tidak diketahui
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Agung Nugrawan KutanaAfiliasi tidak diketahui2
Nisrina Putri HanifahAfiliasi tidak diketahui2
RatnawatiAfiliasi tidak diketahui1
Abdul Rasyid ZartaAfiliasi tidak diketahui1
Teguh Rizali ZahroniAfiliasi tidak diketahui1
Cici AnisaAfiliasi tidak diketahui1
Muhammad Rafli AkbarAfiliasi tidak diketahui1
Jane Secilia WidodoAfiliasi tidak diketahui1
Janice Celsia WidodoAfiliasi tidak diketahui1
Fatmawati AfandiAfiliasi tidak diketahui1
Fransisco Carles GelungAfiliasi tidak diketahui1
Diana KristinAfiliasi tidak diketahui1
Brayen Daniel RajaluhuAfiliasi tidak diketahui1
Martinus YanAfiliasi tidak diketahui1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://journal.unhas.ac.id/index.php/perennial/oai, pertama di-harvest 5 Nov 2026, terakhir terlihat 5 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en">The Improvement of Jabon Wood Density Through The Furfuryl Alcohol and Nano-SiO2: Pengingkatan Kerapatan Kayu Jabon Melalui Impregnasi Furfuril Alkohol dan Nano-SiO2</dc:title>
	<dc:title xml:lang="id">Pengingkatan Kerapatan Kayu Jabon Melalui Impregnasi Furfuril Alkohol dan Nano-SiO2: The Improvement of Jabon Wood Density Through The Furfuryl Alcohol and Nano-SiO2</dc:title>
	<dc:creator xml:lang="en">Wahyuningtyas, Irma</dc:creator>
	<dc:creator xml:lang="id">Wahyuningtyas, Irma</dc:creator>
	<dc:creator xml:lang="id">Dirna, Fitria Cita</dc:creator>
	<dc:subject xml:lang="id">furfuril alkohol</dc:subject>
	<dc:subject xml:lang="id">impregnasi</dc:subject>
	<dc:subject xml:lang="id">jabon</dc:subject>
	<dc:subject xml:lang="id">nano-SiO2</dc:subject>
	<dc:subject xml:lang="id">sifat fisis</dc:subject>
	<dc:subject xml:lang="en">furfuryl alcohol</dc:subject>
	<dc:subject xml:lang="en">impregnation</dc:subject>
	<dc:subject xml:lang="en">jabon</dc:subject>
	<dc:subject xml:lang="en">nano-SiO2</dc:subject>
	<dc:subject xml:lang="en">physical properties</dc:subject>
	<dc:description xml:lang="en">



Jabon (Anthocephalus cadamba Miq.) is a fast-growing wood that is widely utilized by the society as a construction material and furniture making. This study aimed to increase the density of jabon wood through a vacuum pressure impregnation method. Furfuryl alcohol (FA) and nano-SiO2 with three concentrations (0.5%, 0.75%, dan 1%) were used as impregnation additives, with control and FA without nanoparticles as comparisons. Impregnation was initiated with a vacuum (0.5 bar) for an hour, followed by pressure (2.5 bar) for 2 hours. The significant results on the physical properties of jabon wood including weight percent gain (WPG), bulking effect (BE), and density showed the success of the modification treatment through the FA and nano-SiO2 impregnation process with various concentrations, which the wood density increased from 0.60 g/cm3 to 0.94 g/cm3. The composition of FA and 1% nano-SiO2 solution was the best treatment to obtain the highest density in modified jabon wood.



</dc:description>
	<dc:description xml:lang="id">



Kayu jabon (Anthocephalus cadamba Miq.) merupakan kayu cepat tumbuh yang banyak diminati masyarakat untuk dimanfaatkan sebagai bahan konstruksi dan pembuatan furnitur. Penelitian ini bertujuan untuk meningkatkan kerapatan kayu jabon melalui metode impregnasi vakum tekan. Furfuril alkohol (FA) dan nano-SiO2 dengan tiga konsentrasi (0.5%, 0.75%, dan 1%) digunakan sebagai bahan impregnan, dengan kontrol dan perlakuan FA tanpa nanopartikel sebagai pembanding. Impregnasi dimulai dengan pemberian vakum (0.5 bar) selama 1 jam, dilanjutkan dengan tekan (2.5 bar) selama 2 jam. Hasil yang signifikan pada sifat fisis kayu jabon yang meliputi weight percent gain (WPG), bulking effect (BE), dan kerapatan menunjukkan keberhasilan perlakuan modifikasi melalui proses impregnasi FA dan nano-SiO2 dengan berbagai konsentrasi, yang mana kerapatan kayu meningkat dari 0.60 g/cm3 menjadi 0.94 g/cm3. Komposisi larutan FA dan nano-SiO2 1% menjadi perlakuan terbaik untuk mendapatkan nilai kerapatan tertinggi pada kayu jabon termodifikasi.



</dc:description>
	<dc:publisher xml:lang="en">Forestry Faculty of Hasanuddin University</dc:publisher>
	<dc:date>2025-04-30</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://journal.unhas.ac.id/index.php/perennial/article/view/43187</dc:identifier>
	<dc:identifier>10.24259/perennial.v21i1.43187</dc:identifier>
	<dc:source xml:lang="en">PERENNIAL; Vol. 21 No. 1 (2025): Vol. 21 No. 1, April 2025; 24-29</dc:source>
	<dc:source xml:lang="id">PERENNIAL; Vol 21 No 1 (2025): Vol. 21 No. 1, April 2025; 24-29</dc:source>
	<dc:source>2685-6859</dc:source>
	<dc:source>1412-7784</dc:source>
	<dc:language>en</dc:language>
	<dc:language>id</dc:language>
	<dc:relation>https://journal.unhas.ac.id/index.php/perennial/article/view/43187/12757</dc:relation>
</oai_dc:dc>