EFFECT OF WELDING CURRENT ON LOW CARBON STEEL CHARACTERISTICS IN SMAW CLADDING PROCESS

Jurnal Pendidikan Teknik Mesin · Vol. 25 No. 1 (2025) · hlm. 1–7

DOI
10.15294/jptm.v25i1.21279
ISSN
2503-1759, 2503-1759
Terbit
2025-06-30
Penerbit
Universitas Negeri Semarang
Bahasa
eng

Abstrak

The electric current magnitude is a fundamental parameter that directly affects penetration characteristics and weld bead geometry. This study analyzes the effect of current variations on physical and mechanical properties in the cladding process using the Shielded Metal Arc Welding (SMAW) method. The materials used are low-carbon steel and HV-600 electrodes with a diameter of 3.2 mm. The SMAW method was applied with current variations of 100 A, 120 A, 140 A, and 160 A. The tests carried out were NDT liquid penetrant, macro structure, micro structure and Vickers hardness. The results indicate a positive correlation between increasing current and hardness values in the weld area, with the highest hardness recorded at 665.803 HVN at 160 A and the lowest at 515.143 HVN at 100 A. Meanwhile, in the Heat Affected Zone (HAZ), a non-linear pattern was observed, with a maximum hardness of 263.237 HVN at 120 A and a minimum of 219.110 HVN at 140 A. Microstructural analysis revealed the formation of ferrite, pearlite, bainite, and martensite phases in the weld area, providing insights into optimizing welding parameters to enhance the mechanical properties of low-carbon steel cladding.

Kata kunci

Jaringan kolaborasi para penulis

40 penulis · 135 tautan kepenulisan bersama · menampilkan 40 yang paling banyak terhubung

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • University of Technology Malaysia
  • Afiliasi tidak diketahui
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Fajar Perdana NurullahAfiliasi tidak diketahui10
Farid Nanda SyanurAfiliasi tidak diketahui6
Muhamad Fatikul ArifAfiliasi tidak diketahui5
Dimas AldyansyahAfiliasi tidak diketahui4
Didik SupriyadiAfiliasi tidak diketahui3
Rico Aditia PrahmanaAfiliasi tidak diketahui3
Devia Gahana Cindi AlfianAfiliasi tidak diketahui3
M. Farhan SidikAfiliasi tidak diketahui3
Rizky SaputraAfiliasi tidak diketahui3
Gilang Putra WibawaAfiliasi tidak diketahui3
Muhammad SyaukaniAfiliasi tidak diketahui3
Fajri KurniawanUniversity of Technology Malaysia3
Akhmad NurdinAfiliasi tidak diketahui3
Iqbal Zulfikar Alief UtamaAfiliasi tidak diketahui3
Bagus Angger PrasetiyoAfiliasi tidak diketahui3
Rosyidi HidayatAfiliasi tidak diketahui3
KhodraniAfiliasi tidak diketahui3
Sena MaulanaAfiliasi tidak diketahui3
Dicky J. SilitongaAfiliasi tidak diketahui2
Putty YunestiAfiliasi tidak diketahui2
Riyan FerdiyantoAfiliasi tidak diketahui2
Wahyu S. SipahutarAfiliasi tidak diketahui2
Indah PuspitasariAfiliasi tidak diketahui1
Puji BasukiAfiliasi tidak diketahui1
Kuncoro DiharjoAfiliasi tidak diketahui1
Devia G. C. AlfianAfiliasi tidak diketahui1
Dicky Januarizky SilitongaAfiliasi tidak diketahui1
Guna Bangun PersadaAfiliasi tidak diketahui1
Setiadi Wira BuanaAfiliasi tidak diketahui1
Andi Rahadiyan WijayaAfiliasi tidak diketahui1
I Gusti Bagus Budi DharmaAfiliasi tidak diketahui1
Arysca Wisnu SatriaAfiliasi tidak diketahui1
Hida Arliani Nur AnisaAfiliasi tidak diketahui1
Dika Ariyanto AriyantoAfiliasi tidak diketahui1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://journal.unnes.ac.id/journals/JPTM/oai, pertama di-harvest 5 Nov 2026, terakhir terlihat 8 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en">EFFECT OF WELDING CURRENT ON LOW CARBON STEEL CHARACTERISTICS IN SMAW CLADDING PROCESS</dc:title>
	<dc:creator xml:lang="en">paundra, fajar</dc:creator>
	<dc:creator xml:lang="en"> Yasmin, Dzikrina Salsabila </dc:creator>
	<dc:creator xml:lang="en"> Pujiyulianto, Eko</dc:creator>
	<dc:creator xml:lang="en">Muhyi, Abdul</dc:creator>
	<dc:creator xml:lang="en">Rajagukguk, Kardo </dc:creator>
	<dc:creator xml:lang="en">Prabowo, Imam</dc:creator>
	<dc:subject xml:lang="en">Current</dc:subject>
	<dc:subject xml:lang="en">welding</dc:subject>
	<dc:subject xml:lang="en">Cladding</dc:subject>
	<dc:subject xml:lang="en">microstructure</dc:subject>
	<dc:subject xml:lang="en">hardness</dc:subject>
	<dc:description xml:lang="en">The electric current magnitude is a fundamental parameter that directly affects penetration characteristics and weld bead geometry. This study analyzes the effect of current variations on physical and mechanical properties in the cladding process using the Shielded Metal Arc Welding (SMAW) method. The materials used are low-carbon steel and HV-600 electrodes with a diameter of 3.2 mm. The SMAW method was applied with current variations of 100 A, 120 A, 140 A, and 160 A. The tests carried out were NDT liquid penetrant, macro structure, micro structure and Vickers hardness. The results indicate a positive correlation between increasing current and hardness values in the weld area, with the highest hardness recorded at 665.803 HVN at 160 A and the lowest at 515.143 HVN at 100 A. Meanwhile, in the Heat Affected Zone (HAZ), a non-linear pattern was observed, with a maximum hardness of 263.237 HVN at 120 A and a minimum of 219.110 HVN at 140 A. Microstructural analysis revealed the formation of ferrite, pearlite, bainite, and martensite phases in the weld area, providing insights into optimizing welding parameters to enhance the mechanical properties of low-carbon steel cladding.</dc:description>
	<dc:publisher xml:lang="en">Universitas Negeri Semarang</dc:publisher>
	<dc:date>2025-06-30</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://journal.unnes.ac.id/journals/JPTM/article/view/21279</dc:identifier>
	<dc:identifier>10.15294/jptm.v25i1.21279</dc:identifier>
	<dc:source xml:lang="en">Jurnal Pendidikan Teknik Mesin; Vol. 25 No. 1 (2025): June 2025; 1 - 7</dc:source>
	<dc:source>2503-1759</dc:source>
	<dc:source>2503-1759</dc:source>
	<dc:source>10.15294/jptm.v25i1</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://journal.unnes.ac.id/journals/JPTM/article/view/21279/5294</dc:relation>
	<dc:rights xml:lang="en">Copyright (c) 2025 Jurnal Pendidikan Teknik Mesin</dc:rights>
</oai_dc:dc>