Pengaruh Warna Pelapis dan Ketebalan Lapisan Pada Proses Zinc Electroplating Terhadap Laju Korosi Baja AISI 1015

Jurnal Inovasi Mesin · Vol. 3 No. 1 (2021) · hlm. 27–34

DOI
10.15294/jim.v3i1.48940
ISSN
2746-7694
Terbit
2021-04-20
Penerbit
Department of Mechanical Engineering, Faculty of Engineering, Universitas Negeri Semarang
Bahasa
eng

Abstrak

To improve the material's corrosion resistance, metal plating can be done. The main purpose of electroplating is to increase corrosion resistance and beautify the appearance with a variety of colors. The purpose of this study was to examine the effect of coating color variations on the corrosion rate of low carbon steel. The research method used was experimental. Using zinc electroplating and trivalent passivation treatment. Corrosion rate testing using the method weight loss, immersion period of 7 days with 3.5% NaCl corrosive medium. Layer thickness testing was carried out using the micro photo method. The research were obtained by directly observing the experimental results which were presented in tables and graphs. The results showed that there was an effect of coating color variations on the corrosion rate of AISI 1015 steel in the form of a decrease in the corrosion rate of each coating color variation. The lowest corrosion rate is in the black coating 0.016840030 mmpy. The layer thickness also affects the corrosion rate of AISI 1015 Steel. The higher the coating thickness in the process zinc electroplating, the lower the corrosion rate of AISI 1015 Steel.

Jaringan kolaborasi para penulis

40 penulis · 158 tautan kepenulisan bersama · menampilkan 40 yang paling banyak terhubung

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • Cenderawasih University
  • Universitas Stikubank
  • Afiliasi tidak diketahui
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Januar Parlaungan SiregarAfiliasi tidak diketahui9
Tezara CionitaAfiliasi tidak diketahui7
Samsudin AnisAfiliasi tidak diketahui5
Rifky IsmailAfiliasi tidak diketahui5
Al Ichlas ImranAfiliasi tidak diketahui4
Hendrix Noviyanto FirmansyahAfiliasi tidak diketahui4
Rahmat Doni WidodoAfiliasi tidak diketahui4
Jamiluddin JaafarAfiliasi tidak diketahui3
Wirawan SumbodoAfiliasi tidak diketahui3
WahyudiAfiliasi tidak diketahui2
SukarniAfiliasi tidak diketahui2
Sonika MaulanaAfiliasi tidak diketahui2
Agustinus Purna IrawanAfiliasi tidak diketahui2
Yusuf SubagyoAfiliasi tidak diketahui2
Baharudin PriwintokoAfiliasi tidak diketahui2
Athanasius Priharyoto BayusenoAfiliasi tidak diketahui2
Rozanna DewiAfiliasi tidak diketahui2
Mohd Ruzaimi Mat RejabAfiliasi tidak diketahui2
Agung Efriyo HadiAfiliasi tidak diketahui2
Muji SetiyoAfiliasi tidak diketahui2
Khoirul HudaCenderawasih University1
Muhammad Ainun AtharAfiliasi tidak diketahui1
Septian Eko CahyantoAfiliasi tidak diketahui1
Ruben Bayu KristiawanAfiliasi tidak diketahui1
Galih TriLaksonoAfiliasi tidak diketahui1
Agus PrasetyoUniversitas Stikubank1
Risky IsmailAfiliasi tidak diketahui1
A. P. BayusenoAfiliasi tidak diketahui1
Muhammad AfrizalAfiliasi tidak diketahui1
Janviter ManaluAfiliasi tidak diketahui1
Achmad Erlangga Bintang SamodraAfiliasi tidak diketahui1
Abram Puspa PramuditaAfiliasi tidak diketahui1
Sonika Maulana HalimAfiliasi tidak diketahui1
Muhammad Ziddun Ni’amAfiliasi tidak diketahui1
Rizqi Fitri NaryantoAfiliasi tidak diketahui1
Kuat NursiamAfiliasi tidak diketahui1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://journal.unnes.ac.id/sju/index.php/jim/oai, pertama di-harvest 6 Nov 2026, terakhir terlihat 8 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en-US">Pengaruh Warna Pelapis dan Ketebalan Lapisan Pada Proses Zinc Electroplating Terhadap Laju Korosi Baja AISI 1015</dc:title>
	<dc:creator>Haqiqi, Muttaqin</dc:creator>
	<dc:creator>Rusiyanto, Rusiyanto</dc:creator>
	<dc:creator>Fitriyana, Deni Fajar</dc:creator>
	<dc:creator>Kriswanto, Kriswanto</dc:creator>
	<dc:description xml:lang="en-US">To improve the material's corrosion resistance, metal plating can be done. The main purpose of electroplating is to increase corrosion resistance and beautify the appearance with a variety of colors. The purpose of this study was to examine the effect of coating color variations on the corrosion rate of low carbon steel. The research method used was experimental. Using zinc electroplating and trivalent passivation treatment. Corrosion rate testing using the method weight loss, immersion period of 7 days with 3.5% NaCl corrosive medium. Layer thickness testing was carried out using the micro photo method. The research were obtained by directly observing the experimental results which were presented in tables and graphs. The results showed that there was an effect of coating color variations on the corrosion rate of AISI 1015 steel in the form of a decrease in the corrosion rate of each coating color variation. The lowest corrosion rate is in the black coating 0.016840030 mmpy. The layer thickness also affects the corrosion rate of AISI 1015 Steel. The higher the coating thickness in the process zinc electroplating , the lower the corrosion rate of AISI 1015 Steel.</dc:description>
	<dc:publisher xml:lang="en-US">Department of Mechanical Engineering, Faculty of Engineering, Universitas Negeri Semarang</dc:publisher>
	<dc:date>2021-04-20</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en-US">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://journal.unnes.ac.id/sju/jim/article/view/48940</dc:identifier>
	<dc:identifier>10.15294/jim.v3i1.48940</dc:identifier>
	<dc:source xml:lang="en-US">Jurnal Inovasi Mesin; Vol 3 No 1 (2021): APRIL 2021; 27-34</dc:source>
	<dc:source>2746-7694</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://journal.unnes.ac.id/sju/jim/article/view/48940/19726</dc:relation>
</oai_dc:dc>