PENGARUH TREATMENT PANAS (STEAM CURING) DENGAN SUHU 70ºC SELAMA 24 JAM TERHADAP KUAT TEKAN BETON FLY ASH

Media Konstruksi : Jurnal Ilmiah Teknik Sipil · Vol. 4 No. 1 (2019)

DOI
10.33772/jmk.v4i1.27210
ISSN
2503-2712
Published
2019-04-01
Publisher
PRODI D3 TEKNIK SIPIL
Language
eng

Abstract

Abstract The purpose of this study was to determine the compressive strength of concrete by using fly ash as a material for reducing the need for cement in a mixture of variations of 0%, 5%, 10%, 15%, 20%, 25%, and 30% with a treatment temperature of 70ºC for 1 day.This test is a research study in the laboratory by examining fine aggregates and coarse aggregates. In this study the composition of the mixture used is contained in the mix design analysis with K-250 concrete quality with variations in the mixture of fly ash 0%, 5%, 10%, 20%, 25%, and 30% with a treatment temperature of 70 ° c for 24 hours then soak using ordinary water for 28 days using the SNI method.The value of compressive strength of concrete at the age of 7 days using treatment temperature of 70ºC for 24 hours occurred at 15% variation of fly ash levels of 20.78 Mpa and the value of 28-day concrete compressive strength occurred at 25% fly ash levels of 25, 95 Mpa of concrete without fly ash. Abstrak Tujuan dari penelitian ini adalah untuk mengetahui kuat tekan beton dengan menggunakan fly ash sebagai bahan pengurangan kebutuhan semen pada variasi campuran 0%, 5%, 10%, 15%, 20%, 25%, dan 30% dengan perawatan suhu 70ºC selama 1 hari.Pengujian ini merupakan studi penelitian di laboratorium dengan melakukan pemeriksaan agregat halus dan agregat kasar. Pada penelitian ini komposisi campuran yang digunakan yaitu terdapat dalam analisa mix design dengan mutu beton K-250 dengan variasi campuran fly ash 0%, 5 %, 10%, 20%, 25%.dan 30% dengan perawatan suhu70°c selama 24 jam kemudian rendam mengunakan air biasa selama umur 28 hari menggunakan metode SNI.Nilai kuat tekan beton rata-rata pada umur 7 hari dengan menggunakan perawatan suhu 70ºC selama 24 jam terjadi pada variasi kadar fly ash 15% sebesar 20,78 Mpa dan nilai kuat tekan beton umur 28 hari terjadi pada variasi kadar fly ash 25% sebesar 25,95 Mpa dari beton tanpa fly ash.

Collaboration network of the authors

40 authors · 110 co-authorship links · 5 across different organisations · showing the 40 most connected

Hover or tap a name to highlight its co-authors. Double-click to open the author's page.

  • Universitas Halu Oleo
  • Universitas Sembilanbelas November Kolaka
  • University of Mataram
  • Affiliation unknown
  • Different organisations
  • Same organisation
  • Affiliation unknown
  • Thicker line = more joint articles · bigger circle = more articles
Show as table
Co-authorOrganisationJoint articles
Umran SaritaAffiliation unknown3
Fathur Rahman RustanUniversitas Sembilanbelas November Kolaka3
Try Sugiyarto SoeparyantoUniversitas Halu Oleo3
Muammar MakmurUniversitas Halu Oleo3
Baso MursidiAffiliation unknown2
Muhammad Syarif PrasetiaAffiliation unknown2
Aloysius A. Prima MangiriAffiliation unknown2
Fahril AlwanAffiliation unknown2
Billing BillingAffiliation unknown1
I Komang Arya Yogi ParamitaAffiliation unknown1
Anafi MinmahddunUniversitas Halu Oleo1
Putra Dwijanto MangokiUniversitas Halu Oleo1
Wayan MustikaUniversitas Halu Oleo1
Sabil SabilUniversitas Halu Oleo1
Milasari MilasariAffiliation unknown1
Veny AnjarwatiAffiliation unknown1
La Ode Muhamad Nurrakhmad ArsyadUniversitas Halu Oleo1
Mappa NashrunAffiliation unknown1
Imam MulyonoAffiliation unknown1
Agusti FaturrahmanAffiliation unknown1
Ainussalbi Al IkhsanAffiliation unknown1
Arung PatandiananAffiliation unknown1
sulha sulhaAffiliation unknown1
Juprianto JupriantoAffiliation unknown1
Ferdinal FerdinalAffiliation unknown1
Jusmiati JusmiatiAffiliation unknown1
Muh. Rizal AlhasAffiliation unknown1
Wayan MustikaAffiliation unknown1
Irvan JayaAffiliation unknown1
Umran SaritaUniversitas Halu Oleo1
Mappa NashrunUniversitas Halu Oleo1
Laode HajiUniversitas Halu Oleo1
Raymond N. MangiriAffiliation unknown1
Zulkarnain ZulkarnainUniversity of Mataram1
Baso MursidiUniversitas Halu Oleo1
La Ode Rizki DarmawanUniversitas Halu Oleo1
Iramayanti IramayantiAffiliation unknown1

Affiliations come from OpenAlex; journal OAI-PMH metadata carries none. Authors without an OpenAlex ID are matched by name, which can merge or split people.

Metadata source: OAI-PMH (metadata jurnal) https://ojs.uho.ac.id/index.php/MedKons/oai, first harvested 31 Oct 2026, last seen 31 Oct 2026.
Original metadata (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en-US">PENGARUH TREATMENT PANAS (STEAM CURING) DENGAN SUHU 70ºC SELAMA 24 JAM TERHADAP KUAT TEKAN BETON FLY ASH</dc:title>
	<dc:creator>Lucky, Lucky</dc:creator>
	<dc:creator>Tamburaka, Romy S. E.</dc:creator>
	<dc:creator>Mas'ud, Fitriah</dc:creator>
	<dc:description xml:lang="en-US"> Abstract The purpose of this study was to determine the compressive strength of concrete by using fly ash as a material for reducing the need for cement in a mixture of variations of 0%, 5%, 10%, 15%, 20%, 25%, and 30% with a treatment temperature of 70ºC for 1 day .This test is a research study in the laboratory by examining fine aggregates and coarse aggregates. In this study the composition of the mixture used is contained in the mix design analysis with K-250 concrete quality with variations in the mixture of fly ash 0%, 5%, 10%, 20%, 25%, and 30% with a treatment temperature of 70 ° c for 24 hours then soak using ordinary water for 28 days using the SNI method.The value of compressive strength of concrete at the age of 7 days using treatment temperature of 70ºC for 24 hours occurred at 15% variation of fly ash levels of 20.78 Mpa and the value of 28-day concrete compressive strength occurred at 25% fly ash levels of 25 , 95 Mpa of concrete without fly ash.  Abstrak Tujuan dari penelitian ini adalah untuk mengetahui kuat tekan beton dengan menggunakan fly ash sebagai bahan pengurangan kebutuhan semen pada variasi campuran 0%, 5%, 10%, 15%, 20%, 25%, dan 30% dengan perawatan suhu 70ºC selama 1 hari.Pengujian ini merupakan studi penelitian di laboratorium dengan melakukan pemeriksaan agregat halus dan agregat kasar. Pada penelitian ini komposisi campuran yang digunakan yaitu terdapat dalam analisa mix design dengan mutu beton K-250 dengan variasi campuran fly ash 0%, 5 %, 10%, 20%, 25%.dan 30% dengan perawatan suhu70°c selama 24 jam kemudian rendam mengunakan air biasa  selama umur 28 hari menggunakan metode SNI.Nilai kuat tekan beton rata-rata pada umur 7 hari dengan menggunakan perawatan suhu 70ºC selama 24 jam terjadi pada variasi kadar fly ash 15% sebesar 20,78 Mpa dan nilai kuat tekan beton umur 28 hari terjadi pada variasi kadar fly ash 25% sebesar 25,95 Mpa dari beton tanpa fly ash. </dc:description>
	<dc:publisher xml:lang="en-US">PRODI D3 TEKNIK SIPIL</dc:publisher>
	<dc:contributor xml:lang="en-US"></dc:contributor>
	<dc:date>2019-04-01</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en-US">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://ojs.uho.ac.id/index.php/MedKons/article/view/27210</dc:identifier>
	<dc:identifier>10.33772/jmk.v4i1.27210</dc:identifier>
	<dc:source xml:lang="en-US">Media Konstruksi : Jurnal Ilmiah Teknik Sipil; Vol 4, No 1 (2019): MedKons</dc:source>
	<dc:source>2503-2712</dc:source>
	<dc:source>10.33772/jmk.v4i1</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://ojs.uho.ac.id/index.php/MedKons/article/view/27210/15855</dc:relation>
	<dc:rights xml:lang="en-US">Copyright (c) 2022 MEDIA KONSTRUKSI</dc:rights>
</oai_dc:dc>