PEMBUATAN DAN KARAKTERISASI MAGNET KOMPOSIT BERBAHAN DASAR BARIUM FERIT DENGAN PENGIKAT KARET ALAM

Unnes Physics Journal · Vol. 2 No. 2 (2013)

ISSN
2252-6978
Terbit
2013-12-07
Penerbit
Unnes Physics Journal
Bahasa
eng

Abstrak

The creation of magnetic composite materials using barium ferrite with a natural rubber as a binding material has been successfully carried out. Fabricated Barium ferrite and natural rubber with composition (1-x) + barium ferrite + (x) natural rubber, 0.2 ≤ x ≤ 0.5. Mixing was done at room temperature. Mix was built with a pressure of 3 tons. The samples were tested to determine the density and mechanical elastics. Samples with 50% barium ferrite has great appeal that is given weight up to 1,332 kg, but has a smaller density is 1.79 x 10-2 (kg/m3). This Happen because the larger the binder material, the mechanical strength will be stronger. The more barium ferrite magnets remanence are used then the value will be greater. Composition of 80% barium ferrite magnet remanence value is 0.79 (kG) which is best and has a value of coercivity (Hc) of more than 200 Oe. This proves that the magnets are made including hard magnetic.

Jaringan kolaborasi para penulis

40 penulis · 156 tautan kepenulisan bersama · 2 lintas organisasi · menampilkan 40 yang paling banyak terhubung

Arahkan kursor atau ketuk sebuah nama untuk menyorot rekan penulisnya. Klik dua kali untuk membuka halaman penulis.

  • State University of Semarang
  • Diponegoro University
  • Afiliasi tidak diketahui
  • Organisasi berbeda
  • Organisasi sama
  • Afiliasi tidak diketahui
  • Garis lebih tebal = lebih banyak artikel bersama · lingkaran lebih besar = lebih banyak artikel
Tampilkan sebagai tabel
Rekan penulisOrganisasiArtikel bersama
Mahardika Prasetya AjiAfiliasi tidak diketahui7
Budi AstutiAfiliasi tidak diketahui4
Ellianawati EllianawatiState University of Semarang3
. SupriyadiAfiliasi tidak diketahui3
Teguh Hardi RaharjoAfiliasi tidak diketahui2
WidiyantoAfiliasi tidak diketahui2
Upik NurbaitiAfiliasi tidak diketahui2
FiantiAfiliasi tidak diketahui2
Sri Mulyani ESAfiliasi tidak diketahui2
Heri PramonoAfiliasi tidak diketahui2
Sulhadi SulhadiAfiliasi tidak diketahui2
Fatwa Aji KurniawanAfiliasi tidak diketahui2
Sarwi SarwiAfiliasi tidak diketahui2
Putut MarwotoState University of Semarang2
Achmad SopyanAfiliasi tidak diketahui2
SarwiAfiliasi tidak diketahui2
Sutikno SutiknoDiponegoro University1
Ani RusilowatiState University of Semarang1
Sugiyanto SugiyantoAfiliasi tidak diketahui1
Langlang HandayaniAfiliasi tidak diketahui1
Budi Naini MindiyartoAfiliasi tidak diketahui1
Nur’ainiyyah HasniAfiliasi tidak diketahui1
Shelly Salista RahmayantiAfiliasi tidak diketahui1
Candra FanleonAfiliasi tidak diketahui1
Najwa Abel SwastikaAfiliasi tidak diketahui1
Lastri UtamiAfiliasi tidak diketahui1
Indah AnisykurlillahAfiliasi tidak diketahui1
Ahmad NurkhinAfiliasi tidak diketahui1
Indah Fajarini Sri WahyuningrumAfiliasi tidak diketahui1
Hasan MukhibadAfiliasi tidak diketahui1
KusumantoroAfiliasi tidak diketahui1
Saeful BahriAfiliasi tidak diketahui1
Titih NursugihartiAfiliasi tidak diketahui1
Roch Aris HidayatAfiliasi tidak diketahui1
Jahdiah JahdiahAfiliasi tidak diketahui1
Mawar SafeiAfiliasi tidak diketahui1
Dendy RandaAfiliasi tidak diketahui1

Afiliasi berasal dari OpenAlex; metadata OAI-PMH jurnal tidak memuatnya. Penulis tanpa ID OpenAlex dicocokkan berdasarkan nama, sehingga dua orang bisa tergabung atau satu orang bisa terpisah.

Sumber metadata: OAI-PMH (metadata jurnal) https://journal.unnes.ac.id/sju/index.php/upj/oai, pertama di-harvest 6 Nov 2026, terakhir terlihat 6 Nov 2026.
Metadata asli (oai_dc) 
<oai_dc:dc xmlns="http://www.openarchives.org/OAI/2.0/" xmlns:dc="http://purl.org/dc/elements/1.1/" xmlns:oai_dc="http://www.openarchives.org/OAI/2.0/oai_dc/" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance" xsi:schemaLocation="http://www.openarchives.org/OAI/2.0/oai_dc/  http://www.openarchives.org/OAI/2.0/oai_dc.xsd">
	<dc:title xml:lang="en-US">PEMBUATAN DAN KARAKTERISASI MAGNET KOMPOSIT BERBAHAN DASAR BARIUM FERIT DENGAN PENGIKAT KARET ALAM</dc:title>
	<dc:creator>Wicaksono, Rahmawan</dc:creator>
	<dc:creator>Yulianto, Agus</dc:creator>
	<dc:creator>-, Sulhadi</dc:creator>
	<dc:description xml:lang="en-US">The creation of magnetic composite materials using barium ferrite with a natural rubber as a binding material has been successfully carried out. Fabricated Barium ferrite and natural rubber with composition (1-x) + barium ferrite + (x) natural rubber, 0.2 ≤ x ≤ 0.5. Mixing was done at room temperature. Mix was built with a pressure of 3 tons. The samples were tested to determine the density and mechanical elastics. Samples with 50% barium ferrite has great appeal that is given weight up to 1,332 kg, but has a smaller density is 1.79 x 10-2  (kg/m3). This Happen because the larger the binder material, the mechanical strength will be stronger. The more barium ferrite magnets remanence are used then the value will be greater. Composition of 80% barium ferrite magnet remanence value is 0.79 (kG) which is best and has a value of coercivity (Hc) of more than 200 Oe. This proves that the magnets are made including hard magnetic.</dc:description>
	<dc:publisher xml:lang="en-US">Unnes Physics Journal</dc:publisher>
	<dc:date>2013-12-07</dc:date>
	<dc:type>info:eu-repo/semantics/article</dc:type>
	<dc:type>info:eu-repo/semantics/publishedVersion</dc:type>
	<dc:type xml:lang="en-US">Peer-reviewed Article</dc:type>
	<dc:format>application/pdf</dc:format>
	<dc:identifier>https://journal.unnes.ac.id/sju/upj/article/view/2770</dc:identifier>
	<dc:source xml:lang="en-US">Unnes Physics Journal; Vol 2 No 2 (2013)</dc:source>
	<dc:source>2252-6978</dc:source>
	<dc:language>eng</dc:language>
	<dc:relation>https://journal.unnes.ac.id/sju/upj/article/view/2770/2569</dc:relation>
</oai_dc:dc>